Selective hydrogenation of acetylenes in the presence of butadiene and catalyst used in the hydrogenation
AssigneeThe Dow Chemical Company
InventorMark C. Couvillion
Life of this patent
Estimating the term…
Abstract
An improved catalyst for removal of acetylenes from liquid hydrocarbon streams with a minimum loss of diolefinic unsaturation present in said liquid composition is disclosed. The catalytic materials, basically copper metal associated with one or more activator metals are impregnated on a gamma alumina support prepared from an organo aluminum compound. The support has properties not found in alumina prepared from naturally occurring precursors.
Claims6
A catalyst for removing .alpha.-acetylenes from liquid hydrocarbon streams consisting essentially of a mixture of finely divided copper metal and minor amounts of at least one polyvalent activator metal selected from the group consisting of silver, platinum, palladium, manganese, cobalt, nickel, chromium and molybdenum, dispersed on an aluminum oxide support, said support being a gamma alumina as defined by the Joint Committee on Powder Diffraction Standards, #29-63, of high purity having a surface area of between about 68 and about 350 square meters per gram, and 90 to 60 percent of the pores have a pore diameter between about 40 .ANG. and 120 .ANG. and not more than 25 percent nor less than 2 percent have a pore diameter between 1000 .ANG. to 10,000 .ANG., a silicone content as SiO.sub.2 of less than about 0.15 weight %, a sodium content as Na.sub.2 O of less than about 0.15 weight %, a sulfur content less than about 0.01 weight % and an iron content as Fe.sub.2 O.sub.3 of less than about 0.06 weight %, said gamma alumina may contain up to 35% by weight of alpha alumina.
A catalyst for removing .alpha.-acetylenes from liquid hydrocarbon streams consisting essentially of a support having thereon a mixture of finely divided copper metal and minor amounts of at least one polyvalent activator metal selected from the group consisting of silver, platinum, palladium, manganese, cobalt, nickel, chromium and molybdenum, said support being a substantially high purity gamma alumina as defined by the Joint Committee on Powder Diffraction Standards #29-63, having a surface area of at least about 68 to about 350 square meters per gram, and 90 to 60 percent of the pores have a pore diameter between about 40 .ANG. and 120 .ANG. and not more than 25 percent nor less than 2 percent have a pore diameter between 1000 .ANG. to 10,000 .ANG., and having a sodium content less than about 0.15% and SiO.sub.2 being less than 0.15% and which may contain up to 35% by weight of alpha alumina.
A catalyst for removing .alpha.-acetylenes from liquid hydrocarbon streams consisting essentially of a support having thereon a mixture of finely divided copper metal and minor amounts of at least one polyvalent activator metal selected from the group consisting of silver, platinum, palladium, manganese, cobalt, nickel, chromium and molybdenum, said support being a substantially high purity gamma alumina as defined by the Joint Committee on Powder Diffraction Standards #29-63, having a surface area of at least about 68 to about 350 square meters per gram, and 90 to 60 percent of the pores have a pore diameter between about 40 .ANG. and 120 .ANG. and not more than 25 percent nor less than 2 percent have a pore diameter between 1000 .ANG. to 10,000 .ANG., and having a sodium content less than about 0.15% and SiO.sub.2 being less than 0.15%, and which may contain up to 35% by weight of alpha alumina, said copper metal being present in from about 3 to 13 weight percent of the support and said combined weight of said activator metals being from 0 to about 15 percent of the copper metal.
A catalyst for removing .alpha.-acetylenes from liquid hydrocarbon streams consisting essentially of a support having thereon a mixture of finely divided copper metal and minor amounts of at least one polyvalent activator metal selected from the group consisting of silver, manganese, cobalt, nickel, and chromium, said support being a substantially high purity gamma alumina as defined by the Joint Committee on Powder Diffraction Standards #29-63, having a surface area of at least about 68 to about 350 square meters per gram, and 90 to 60 percent of the pores have a pore diameter between about 40 .ANG. and 120 .ANG. and not more than 25 percent nor less than 2 percent have a pore diameter between 1000 .ANG. to 10,000 .ANG., and having a sodium content less than about 0.15% and SiO.sub.2 being less than 0.15% and which may contain up to 35% by weight of alpha alumina, said copper metal being present in from about 3 to 13 weight percent of the support and said combined weight of said activator metals being from 0 to about 15 percent of the copper metal, said catalytic metal being applied to said support by reduction of the metal nitrate salts of an aqueous solution composed of
- ______________________________________ Cu(NO.sub.3).sub.2.21/2H.sub.2 O .9135 parts by weight Ni(NO.sub.3).sub.2.6H.sub.2 O .0323 Mn(NO.sub.3).sub.2 50% active .0250 AgNO.sub.3 .0016 Cr(NO.sub.3).sub.3.9H.sub.2 O .0137 Co(NO.sub.3).sub.2.6H.sub.2 O .0137 ______________________________________
- in sufficient water of a pH of 6.5-7.5 to wet the surface of said support.
A catalyst for removing .alpha.-acetylenes from liquid hydrocarbon streams consisting essentially of a support having thereon a mixture of finely divided copper metal and minor amounts of at least one polyvalent activator metal selected from the group consisting of silver, manganese, cobalt, nickel, and chromium, said support being a substantially high purity gamma alumina as defined by the Joint Committee on Powder Diffraction Standards #29-63, having a surface area of at least about 68 to about 350 square meters per gram, and 90 to 60 percent of the pores have a pore diameter between about 40 .ANG. and 120 .ANG. and not more than 25 percent nor less than 2 percent have a pore diameter between 1000 .ANG. to 10,000 .ANG., and having a sodium content less than about 0.15% and SiO.sub.2 being less than 0.15% and which may contain up to 35% by weight of alpha alumina, said copper metal being present in from about 3 to 13 weight percent of the support and said combined weight of said activator metals being from 0 to about 15 percent of the copper metal, said catalytic metal being applied to said support by reduction of the metal nitrate salts of an aqueous solution composed of
- ______________________________________ Cu(NO.sub.3).sub.2.21/2H.sub.2 O .9164 parts by weight Ni(NO.sub.3).sub.2.6H.sub.2 O .0311 Mn(NO.sub.3).sub.2 50% active .0262 AgNO.sub.3 .0016 Cr(NO.sub.3).sub.3.9H.sub.2 O .0131 Co(NO.sub.3).sub.2.6H.sub.2 O .0131 ______________________________________
- in sufficient water of a pH of 6.5-7.5 to wet the surface of said support.
Dependencies are inferred from the claim text.