Abstract

A process for producing an iron oxide weighting material from an iron chloride solution. The iron chloride solution is introduced into an elevated temperature reactor as an atomized mist. The moisture is evaporated from the mist to form iron chloride solids which then react with the steam produced during the evaporation to form particulate iron oxides and hydrogen chloride gas. The iron oxides then are compacted and introduced into a calcination zone maintained at a temperature in the range of from about 400.degree. C. to about 1300.degree. C. The compacted iron oxide is calcined to reduce the surface area of the particles. The calcined iron oxide then is ground to a predetermined particle size.

Claims4

Dependent claims

A process for preparing a weighting material adapated for use in a drilling fluid which comprises:

A. compacting a particulate iron oxide byproduct formed during the regeneration of aqueous hydrochloric acid from an iron chloride solution to reduce the porosity thereof and to increase the pour density thereof to at least 85 pounds per cubic foot and the tap density thereof to at least 100 pounds per cubic foot,
B. calcining said compacted iron oxide byproduct at temperatures in the range of from about 900.degree. C. to about 1300.degree. C. for a period of time sufficient to sinter said compacted iron oxide byproduct and reduce the surface area of said byproduct to less than about 10 square meters per gram and thereafter
C. grinding said calcined byproduct to a predetermined particle size.