Process for the preparation of filaments of high tensile strength and modulus
AssigneeStamicarbon B.V.
InventorsPaul Smith, Pieter J. Lemstra
Life of this patent
Estimating the term…
Abstract
The invention relates to the preparation of filaments with a high tensile strength and a high modulus and to the filaments thus prepared. A solution of a linear polyethylene with a weight-average molecular weight of at least 4.times.10.sup.5 is spun and the filaments, from which the solvent may have been removed in whole or in part, are drawn using a draw ratio of at least (12.times.10.sup.6 /M.sub.w)+1. The filaments are drawn at a temperature such that the modulus is at least 20 GPa. The invention allows filaments to be prepared at high drawing rates, of 0.5 sec.sup.-1 or more, with a modulus of at least 20 GPa and a tensile strength of at least 1 GPa.
Claims6
Process for the preparation of polyethylene filaments of high modulus and tensile strength which comprises spinning a solution having a concentration of from 1% to 20% by weight of a high-molecular-weight linear polyethylene polymer with a weight-average molecular weight of M.sub.w of at least 8.times.10.sup.5, and thereafter drawing the spun filaments using a draw ratio of at least (12.times.10.sup.6 /M.sub.w)+1, at a drawing temperature of between 75.degree. to 135.degree. C. such that, at the draw ratio, concentration and temperature used, the modulus of the filaments is at least 20 GPa.
A process for the preparation of polyethylene filaments of high modulus and tensile strength which consists essentially in spinning a solution having a concentration of from 1% to 20% of high molecular weight linear polyethylene polymer, said polymer having a weight-average molecular weight M.sub.w of at least about 8.times.10.sup.5, using a hydrocarbon or halogenated hydrocarbon solvent having a boiling range at atmospheric temperature of from about 100.degree. C. to about 250.degree. C., the temperature of said solution during spinning being from about 100.degree. C. to about 240.degree. C., spinning said filament through a spinning aperture having a major cross-sectional dimension of from about 0.2 mm to about 2 mm, and thereafter drawing the spun filaments at a temperature between about 75.degree. C. up to about 135.degree. C., at a drawing speed from about 0.5 sec.sup.-1 to 1 sec.sup.-1, and using a draw ratio of at least (12.times.10.sup.6 /M.sub.w)+1, the drawing temperature and drawing ratio used being selected together so that the modulus of the filaments is at least about 20 GPa and up to 100 GPa.
Process for the preparation of polyethylene filaments of high modulus and tensile strength which comprises spinning a solution having a concentration of from 1% to 10% by weight of high-molecular-weight linear polyethylene polymer with a weight-average molecular weight of M.sub.w of at least 8.times.10.sup.5, and thereafter drawing the spun filaments using a draw ratio of at least (12.times.10.sup.6 /M.sub.w)+1, at a drawing temperature of between 75.degree. to 135.degree. C. such that, at the draw ratio, concentration and temperature used, the modulus of the filaments is at least 30 GPa.
Dependencies are inferred from the claim text.