Controlling scale composition during acid pressure leaching of laterite and garnierite ore

In a method for controlling the scaling of autoclave and leaching equipment surfaces in the sulfuric acid leaching of nickeliferous ore containing, in addition to nickel, oxides and silicates of aluminum, iron, and magnesium, the magnesium content of the ore being less than about 4% by weight, wherein during high-pressure leaching of nickeliferous ore feed material fed to a multi-stage autoclave maintained at a temperature ranging from about 180.degree. C. to 300.degree. C. at which scaling occurs containing substantial amounts of alunite, the improvement which comprises:

• controlling the magnesium content of at least a portion of the ore feed material fed to the autoclave to a level of at least about 5% by weight of magnesium and at a pulp density to provide a concentration of magnesium sulfate in the leach liquor at least sufficient to inhibit the formation of alunite scale while favoring the formation of scale containing substantial amounts of magnesium as magnesium sulfate characterized by being soluble in water or dilute sulfuric acid and thereby of being easily removed by chemical dissolution.

A method of controlling the scaling of autoclave and leaching equipment surfaces in the high-pressure sulfuric acid leaching of nickeliferous ores containing, in addition to nickel, oxides and silicates of aluminum, iron, and magnesium, wherein the high-pressure leach is carried out on an ore feed material charged to an autoclave while the autoclave is maintained at an elevated temperature in the range of about 180.degree. C. to 300.degree. C., a pressure of about 130 psig to 1230 psig at an acid-to-ore ratio of about 0.15 to 0.8, during which scaling occurs which comprises:

• controlling the magnesium content of at least a portion of the ore feed to a relatively high level falling within the range of about 3% to 30% by weight to provide a concentration of magnesium in the sulfuric acid solution during ore dissolution at a level sufficient to inhibit the formation of scale containing substantial amounts of alunite while favoring the formation of scale containing substantial amounts of magnesium as magnesium sulfate, and
• removing said scale by contacting said scale with an aqueous solution containing up to about 100 gpl H.sub.2 SO.sub.4 at a temperature of about 50.degree. C. to 250.degree. C.

In a method for controlling the scaling of autoclave and leaching equipment surfaces in the sulfuric acid leaching of nickeliferous ore containing, in addition to nickel, oxides and silicates of aluminum, iron, and magnesium, the magnesium content of the ore being less than about 4% by weight, wherein during high-pressure leaching of nickeliferous ore feed material fed to an autoclave maintained at a temperature ranging from about 180.degree. C. to 300.degree. C., and a pressure of about 130 psig to 1230 psig at an acid-to-ore ratio of about 0.4 to 1 to 0.8 to 1, scaling occurs containing substantial amounts of alunite, the improvement which comprises:

• controlling the magnesium content of at least a portion of the ore feed material fed to the autoclave to a level of at least about 5% by weight of magnesium and at an ore feed pulp density sufficient to provide an amount of magnesium sulfate in the leach liquor at least sufficient to inhibit the formation of alunite scale while favoring the formation of scale containing substantial amounts of magnesium as magnesium sulfate, and
• removing said scale by contacting said scale with an aqueous solution containing up to about 100 gpl H.sub.2 SO.sub.4 at a temperature of about 50.degree. C. to 250.degree. C.