Fiber-reinforced cement, and process
OwnerJose M. Restrepoinventor
Life of this patent
Estimating the term…
Abstract
A hydraulic cement mortar comprising uniformly dispersed reinforcing fibrillated plastic filaments having microfibrillated structure and elements manufactured therefrom have improved mechanical isotropic properties, such as enhanced performance regarding their semi-elastic limit and impact loading characteristics. It is disclosed also the process for manufacturing said elements.
Claims12
A cement mortar consisting essentially of:
- water, particulate mortar components of cement and sand, and separate reinforcing filaments consisting essentially of filaments obtained from polyolefin film,
- said separate microfibrillated filaments consisting in sections shredded from non-twisted fibrillated ribbons having a length of up to 50 mm long, with said fibrillated ribbons having been split apart from said polyolefin film and subjected to microfibrillation by stirring particulate mortar components and said reinforcing filaments to effect stretching the fibrillated film fibrils to breakage so generating smaller splinters which are the microfibrils,
- wherein said separate reinforcing filaments have filamentary structure comprising hooked microfibrils laterally branching from points along the length of said separate filaments, and
- wherein separate reinforcing plastic filaments are evenly distributed throughout the body of said cement mortar in a randomly oriented fashion along all of its spatial directions.
A cement mortar comprising microfibrillated reinforcing filaments obtained from a polyolefin film, wherein said filaments are separate sections of fiber having a length of up to about 50 mm long, with said separate filament sections being provided with curled microfibrils laterally branching out along the length thereof;
- and wherein said separate filaments are homogeneously dispersed throughout said cement mortar in randomly directed orientations in all of its spatial directions using high-speed stirring, and where the filamentary reinforcing material is comprised in an amount between 0.2% and 15% by volume of the total dry volume of non-reinforced mortar.
An isotropic element manufactured from a cement mortar comprising about 0.2%-15% by volume of microfibrillated fiberous reinforcing material over total dry volume comprised of separate filaments evenly distributed throughout the matrix of said element, wherein said filaments are randomly dispersed in all of the spatial directions of said element, with said filaments being separate sections of about 50 mm long cut from fibrillated polyolefin film and subjected to a microfibrillation operation, and with said separate filaments being provided with laterally extending curled or hooked microfibrils branching from points spaced along the length thereof, whereby said element shows substantially equal mechanical properties when measured in any directions of the body thereof.
A method of manufacturing a cement mortar-based, plastic fiber-reinforced element showing mechanical properties which are independent of the direction of its body in which the properties are measured, which method comprises embodying into the cement mortar from about 0.20% by volume to about 15% by volume of fibrous reinforcing plastic material comprised of a fibrillated polyolefin;
- shredding the mortar-fibrous mix to form thereby separate filaments of about 50 mm long homogeneously dispersed throughout said mix while at the same time said separate filaments are given a microfibrillated structure having laterally extended curled or hooked microfibrils branching from points spaced along the length thereof;
- and molding said mortar-fibrous material mix into any element shape with said reinforcing microfibrillated structures being randomly oriented throughout the hardened matrix.
A process for producing cement mortar-based elements having mechanical properties substantially equal in all of the directions of their bodies which comprises the steps of:
- preparing non-twisted, fibrillated ribbons from a polyolefin film material and cutting the fibrillated ribbons into sections of up to about 50 mm long;
- spreading out said fibrillated cut ribbons by air treating the same;
- feeding said sections of open-up fibrillated cut ribbon sections into a mixing device provided with high-speed rotary stirring means while at the same time cement, fine aggregate and water are being fed into said mixing device, and stirring the mix for a time enough to bring about by means of the shredding action between said mix particulate materials and said ribbons separate microfibrillated filaments having microfibrillated structure provided with curled or hooked microfibrils branching therealong, with said microfibrillated filaments being homogeneously distributed throughout the mass of said cement mortar mix, and in orientations randomly directed along all of its spatial directions;
- and,
- molding said cement mortar containing said microfibrillated filaments, into the shape of said elements.
Dependencies are inferred from the claim text.