Bromine-containing polymer and process of preparing a bromine-containing polymer
AssigneeStamicarbon B.V.
InventorsHendrikus C. J. de Man, Petrus T. J. L. Smids
Life of this patent
Estimating the term…
Abstract
Fire-resistant copolymers of bromostyrene and another monomer, preferably acrylonitrile, are made by emulsion polymerization to produce copolymers having 95 to 25 weight percent bromostyrene, the balance being the second monomer. The resulting copolymers have a high bromine content in the range 20 to 44 weight percent and may be used as such as a flame-resistant plastics material or admixed with other plastics such as the polyolefins to impart fire-resistance to the mixture. The copolymers produced exhibit good mechanical properties and fire-resistance values.
Claims8
A process of preparing a bromine-containing copolymer comprising adding 25 to 100 parts by weight of bromostyrene, continuously or in batches, to an aqueous emulsion of 5 to 40 parts by weight of acrylonitrile, and an emulsifier, conducting the polymerization reaction in the presence of an initiator providing water-soluble free radicals and after completion of the polymerization yielding a copolymer product having 60 to 95% by weight of copolymerized bromostyrene therein and having a weight-average molecular weight in the range of 25,000 to 2,000,000.
A process of preparing a bromine-containing copolymer comprising
- (1) preparing an emulsion containing 5 to 40 parts by weight of acrylonitrile, 60 to 95 parts by weight of bromostyrene, an initiator providing water-soluble free radicals and an emulsifier;
- (2) heating from about 10 to about 40% of the emulsion of step (1) to the reaction temperature in a polymerization reactor, and thereafter
- (3) polymerizing the remaining portion of the emulsion while supplying same to the reactor at a rate lower than that at which said polymer is formed;
- and
- (4) recovering the bromine-containing copolymer thus formed, the resulting copolymer having a weight-average molecular weight in the range of 25,000 to 2,000,000.
Dependencies are inferred from the claim text.