Process for heat treatment of a metal workpiece
OwnerWillard E. Kempinventor
Life of this patent
Estimating the term…
Abstract
A process for heat treatment of a metal workpiece, such as a casting (steel, aluminum based alloy or white cast iron). The casting is heated in a fluidized particulate bed (sand) to a relatively constant first temperature. Then, the casting is held (e.g., 3 hours) tightly packed against shape changes in the unfluidized bed until internal structural changes have occurred. Next, the casting is cooled in a fluidized particulate bed (sand) to a relatively constant second temperature. Then, the casting is held (e.g., 3 hours) tightly packed in the unfluidized bed until the desired internal structural changes are completed. The casting is removed from the bed for utilization as a heat treated product.
Claims2
A process for malleabilizing a white iron casting, comprising the steps of:
- (a) subjecting the casting to a fluidized particulate bed at a temperature of about 1750.degree. F. until the casting is heated throughout to substantially this temperature;
- (b) terminating fluidization of the bed and leaving the casting therein for a period of several hours whereby the casting remains packed in a bed at a relatively constant temperature of about 1750.degree. F. as its combined carbon undergoes graphitization;
- (c) subjecting the casting to a fluidized particulate bed at a temperature of about 1400.degree. F. until the casting is cooled rapidly throughout to substantially this temperature;
- (d) terminating fluidization of the bed and leaving the casting packed therein tightly to prevent changes in the external shape and at a relatively constant temperature of about 1400.degree. F. for a sufficient time period for completing the desired conversion of its combined carbon to graphite;
- (e) removing the casting from the bed for subsequent utilization;
- and
- (f) wherein in steps (b) and (d), each bed is subject to vibration to tightly pack the bed material about the casting therein.
A process for malleabilizing a white iron casting, comprising the steps of:
- (a) subjecting the casting to a fluidized particulate bed at a temperature of about 1750.degree. F. until the casting is heated throughout to substantially this temperature;
- (b) terminating fluidization of the bed and leaving the casting therein for a period of several hours whereby the casting remains packed in the bed at a relatively constant temperature of about 1750.degree. F. as its combined carbon undergoes graphitization;
- (c) subjecting the casting to a fluidized particulate bed at a temperature of about 1400.degree. F. until the casting is cooled rapidly throughout to substantially this temperature;
- (d) terminating fluidization of the bed and leaving the casting packed therein tightly to prevent changes in its external shape and at a relatively constant temperature of about 1400.degree. F. for a sufficient time period for completing the desired conversion of its combined carbon to graphite;
- (e) removing the casting from the bed for subsequent utilization;
- and
- (f) wherein in steps (b) and (d), each bed is subject to a reduced pressure condition to tightly pack the bed material about the casting therein.