# US 4,400,292 A · Process for making agents for desulfurizing crude iron or steel melts

> Agents: this data is available as JSON from the patentgrep API and MCP server — see https://patentgrep.com/llms.txt

- Number: US 4,400,292 A
- Document ID: US4400292A
- Status: Granted
- Kind: A
- Application number: 06/359,229
- Filed: 1982-03-18
- Granted: 1983-08-23
- Earliest claimed: 1981-03-24
- Assignees: Hoechst Aktiengesellschaft
- Inventors: Albert Braun; Willi Portz; Georg Strauss; Hans-Martin Delhey
- Web page: https://patentgrep.com/patent/US4400292A

## CPC

- C21C 1/025: {Agents used for dephosphorising or desulfurising}
- C21C 7/0645: {Agents used for dephosphorising or desulfurising}
- C21C: PROCESSING OF PIG-IRON, e.g. REFINING, MANUFACTURE OF WROUGHT-IRON OR STEEL; TREATMENT IN MOLTEN STATE OF FERROUS ALLOYS

## Abstract

The disclosure relates to a process for the manufacture of desulfurizing agents containing 1-6 weight % chemically combined water, based on calcium oxide and carbon-containing calcium carbide, for crude iron and steel melts. More particularly, the disclosure provides for a molten mixture of calcium carbide and calcium oxide containing 20 to 80 weight % CaO to be made from lime and coke; for the mixture to be allowed to cool and solidify into a block; for the solidified block while it still has an average temperature of more than 400.degree. C. to be crushed to particles with a size of less than 150 mm; for the comminuted mixture, which still has a temperature of at least 400.degree. C. to be admixed with a quantity of calcium oxide necessary to establish in the resulting mixture a total content of CaO corresponding to the CaO content desired in the end product; and for the mixture to be gound while intensively mixing it with free carbon and carbonate in the presence of air or nitrogen with a moisture content of 5 to 20 g/m.sup.3 (at 1.013 bar and 273.15 K.) at temperatures below 100.degree. C. to particles with a size of less than 10 mm.

## Claims

### Claim 1

A process for the manufacture of desulfurizing agents containing 1-6 weight % chemically combined water, based on calcium oxide and carbon-containing calcium carbide, for crude iron and steel melts, which comprises: producing from lime and coke a molten mixture of calcium carbide and calcium oxide containing 20 to 80 weight % CaO; allowing the mixture to cool and solidify into a block; rough-crushing the solidified block while it still has an average temperature of more than 400.degree. C. to particles with a size of less than 150 mm; admixing the comminuted mixture, which still has a temperature of at least 400.degree. C., with a quantity of calcium oxide necessary to establish in the resulting mixture a total content of CaO corresponding to the CaO content desired in the end product; and then grinding the mixture while intensively mixing it with free carbon and carbonate in the presence of air or nitrogen with a moisture content of 5 to 20 g/m.sup.3 (at 1.013 bar and 273.15K) at temperatures below 100.degree. C. to particles with a size of less than 10 mm.

### Claim 2 (depends on 1)

A process as claimed in claim 1, wherein the final product contains 0.5 to 8 weight % free carbon and 0.5 to 20 weight % carbonates of calcium, magnesium or sodium.

### Claim 3 (depends on 1)

A process as claimed in claim 1, wherein coarse particles of CaO with a size of 8 to 60 mm are added to the rough-crushed mixture.

### Claim 4 (depends on 1)

A process as claimed in claim 1, wherein a quantity of CaO sufficient to produce a mixture containing more than 45 up to 90 weight % CaO, is added to the rough-crushed mixture.

### Claim 5 (depends on 1)

A process as claimed in claim 1, wherein the mixture is rough-crushed at temperatures of between 400.degree. C. and the solidification temperature.

### Claim 6 (depends on 1)

A process as claimed in claim 1, wherein the molten feed mixture of calcium carbide and calcium oxide with a CaO content of 20 to 45% by weight is produced from lime and coke in customary manner by thermal treatment.

### Claim 7 (depends on 1)

A process as claimed in claim 1, wherein the molten feed mixture of calcium carbide and calcium oxide with a CaO content of more than 45 up to 80 weight % is produced by introducing finely divided calcium oxide into an existing calcium carbide melt containing up to 45 weight % of CaO until establishment therein of a CaO content of at most 80 weight %, and then allowing the whole to solidify into a block.

### Claim 8 (depends on 1)

A process as claimed in claim 1, wherein the mixture is ground at 10.degree.-50.degree. C. to particles with a size of less than 10 mm.

### Claim 9 (depends on 1)

A process as claimed in claim 1, wherein the mixture is ground to particles with a size of less than 0.1 mm.