# US 4,399,263 A · Modification of ethylene/acrylate/carboxylic polymer

> Agents: this data is available as JSON from the patentgrep API and MCP server — see https://patentgrep.com/llms.txt

- Number: US 4,399,263 A
- Document ID: US4399263A
- Status: Granted
- Kind: A
- Application number: 06/334,160
- Filed: 1981-12-24
- Granted: 1983-08-16
- Earliest claimed: 1981-12-24
- Assignees: E. I. Du Pont de Nemours and Company
- Inventors: Nicolas Brodoway
- Web page: https://patentgrep.com/patent/US4399263A

## CPC

- C08K 5/17: Amines; Quaternary ammonium compounds
- C08F 8/32: by reaction with amines
- C08F 2800/20: as weight or mass percentages
- C08K: Use of inorganic or non-macromolecular organic substances as compounding ingredients (paints, inks, varnishes, dyes, polishes, adhesives C09)
- C08F: MACROMOLECULAR COMPOUNDS OBTAINED BY REACTIONS ONLY INVOLVING CARBON-TO-CARBON UNSATURATED BONDS

## Abstract

Elastomeric ethylene/alkyl acrylate/1,4-butenedioic acid ester copolymers are stabilized against variations in cure characteristics by reaction of such polymers with amines, perferably during isolation of such polymers. In addition, substantial increase in the molecular weight of such polymers is achieved if the amines are di- or polyamines.

## Claims

### Claim 1

A process for increasing the hydrolytic stability and uniformity, and optionally increasing the molecular weight of random ethylene/methyl acrylate/1,4-butenedioic acid ester copolymer, said copolymer containing 0.5-10 weight percent 1,4-butenedioic acid ester, 40-62 weight percent methyl acrylate, and 28-59.5 weight percent ethylene, said process comprising heating said copolymer to a temperature of 140.degree.-200.degree. C. for a period of at least five minutes, and then contacting the heated copolymer in which the anhydride content is about 0.01-0.1 mole/kg of said heated copolymer with 0.01-0.1 equivalents of amine per kilogram of polymer wherein the amine consists of carbon, hydrogen and nitrogen atoms and is selected from the group consisting of monamines, polyamino compounds, compounds which generate such monoamines and polyamino compounds upon chemical reaction, and mixtures of the above.

### Claim 2 (depends on 1)

The process of claim 1 wherein the ethylene/alkyl acrylate/1,4-butenedioic acid ester copolymer is heated to 150.degree.-180.degree. C. for 5-15 minutes.

### Claim 3 (depends on 1)

The process of claim 1 wherein the amine is a mixture of mono- and diamines.

### Claim 4 (depends on 1)

The process of claim 1 wherein the amine is selected from the group consisting of dibutylamine, hexamethylenediamine, ethylenediamine, methylenedianiline, diethylenetriamine, tetraethylenepentamine and mixtures of the above.

### Claim 5 (depends on 1)

The process of claim 1 wherein the amine is a mixture of hexamethylenediamine and dibutylamine.

### Claim 6 (depends on 1)

The process of claim 1 wherein the copolymer is contacted with 0.014-0.02 equivalents of amine per kilogram of polymer.