# US 4,399,260 A · Increasing the reactivity of coupling of block polymers > Agents: this data is available as JSON from the patentgrep API and MCP server — see https://patentgrep.com/llms.txt - Number: US 4,399,260 A - Document ID: US4399260A - Status: Granted - Kind: A - Application number: 06/337,037 - Filed: 1982-01-04 - Granted: 1983-08-16 - Earliest claimed: 1982-01-04 - Assignees: The Goodyear Tire & Rubber Company - Inventors: William G. Carson - Web page: https://patentgrep.com/patent/US4399260A ## CPC - C08F 297/044: {using a coupling agent} - C08F: MACROMOLECULAR COMPOUNDS OBTAINED BY REACTIONS ONLY INVOLVING CARBON-TO-CARBON UNSATURATED BONDS ## Abstract There is disclosed a process for the preparation of thermoplastic block polymers which comprises contacting conjugated diolefinic monomers selected from the group consisting of isoprene, piperylene, 2-ethyl-1,3-butadiene, 2,3-dimethyl-1,3-butadiene and 1,3-butadiene, and the like, mixed with at least one polyvinyl aromatic coupling compound selected from the group of o, m and p-divinylbenzene, 1,2,4-trivinylbenzene, 1,8-divinylnaphthalene, 1,2-divinyl-3,4-dimethylbenzene, 2,4-divinylbiphenyl, 3,5,4'-trivinylbiphenyl and 1,3,5-trivinylbenzene under solution polymerization conditions with a polystyryllithium catalyst which has been prepared by reacting an alkyllithium compound with a styrene monomer selected from the group consisting of styrene, alpha-methylstyrene, p-methylstyrene, p-t-butylstyrene, 3-methylstyrene, 1-vinylnaphthalene, and the like, in which an amount of polyvinyl aromatic coupling compound ranges from about 1.0 to about 6 vinyl groups of the polyvinyl aromatic coupling compound per mole of active lithium catalyst used, in which the living block copolymer is treated with (A) a polar compound selected from the group consisting of ethylene glycol dimethyl ether (glyme), diethylene glycol dimethyl ether (diglyme), triethylene glycol dimethyl ether (triglyme), tetraethylene glycol dimethyl ether tetraglyme), 2,3-dimethoxybutane, N,N,N',N'-tetramethylethylene-diamine (TMEDA), tri-n-butylphosphine and hexamethylphosphoric triamide (HMPA), in which the molar ratio of the said polar compounds to the active lithium ranges from about 0.01/1 to about 20/1 or (B) a polar compound selected from the group consisting of tetrahydrofuran, diethyl ether, triethylamine, 1,4-diazabicyclo-2.2.2-octane (DABCO), p-dioxane, tri-n-butylamine and N,N'-dimethylpiperazine, in which the molar ratio of the said polar compounds to the active lithium ranges from about 0.5/1 to about 100/1. ## Claims ### Claim 1 A process for the preparation of thermoplastic block polymers which comprises contacting conjugated diolefinic monomers selected from the group consisting of isoprene, piperylene, 2-ethyl-1,3-butadiene, 2,3-dimethyl-1,3-butadiene and 1,3-butadiene, mixed with at least one polyvinyl aromatic coupling compound selected from the group consisting of o, m and p-divinylbenzene, 1,2,4-trivinylbenzene, 1,8-divinylnaphthalene, 1,2-divinyl-3,4-dimethylbenzene, 2,4-divinylbiphenyl, 3,5,4'-trivinylbiphenyl and 1,3,5-trivinylbenzene under solution polymerization conditions with a polystyryllithium catalyst which has been prepared by reacting an alkyllithium compound with a styrene monomer selected from the group consisting of styrene, alpha-methylstyrene, p-methylstyrene, p-t-butylstyrene, 3-methylstyrene, 1-vinylnaphthalene, in which an amount of polyvinyl aromatic coupling compound ranges from about 1.0 to about 6 vinyl groups of the polyvinyl aromatic coupling compound per mole of active lithium catalyst used, to produce a living polymer and then subsequently contacting said living polymer with (a) a polar compound selected from the group consisting of ethylene glycol dimethyl ether, diethylene glycol dimethyl ether, triethylene glycol dimethyl ether, tetraethylene glycol dimethyl ether, 2,3-dimethyoxybutane, N,N,N',N'-tetramethylethylenediamine, tri-n-butylphosphine and hexamethylphosphoric triamide, in which the molar ratio of the said polar compounds to the active lithium, based on the amount of said polystyryllithium catalyst present at the start of the polymerization, ranges from about 0.01/1 to about 20/1 or (B) a polar compound selected from the group consisting of tetrahydrofuran, diethyl ether, triethylamine, 1,4-diazabicyclo-2.2.2-octane, p-dioxane, tri-n-butylamine and N,N'-dimethylpiperazine, in which the molar ratio of the said polar compounds to the active lithium, based on the amount of said polystyryllithium catalyst present at the start of the polymerization, ranges from about 0.5/1 to about 100/1. ### Claim 2 (depends on 1) A process according to claim 1 in which the conjugated diolefin is butadiene or isoprene. ### Claim 3 (depends on 1) A process according to claim 1 in which the polystyryllithium is prepared from styrene or alphamethylstyrene and n-butyllithium or sec-butyllithium. ### Claim 4 (depends on 1) A process according to claim 1 in which the polar compound of (A) is glycol dimethyl ether, diethyl glycol dimethyl ether or N,N,N',N'-tetra-methylethylenediamine. ### Claim 5 (depends on 1) A process according to claim 1 in which the polar compound of (A) is tetrahydrofuran or 1,4-di-azabicyclo-2.2.2-octane. ### Claim 6 (depends on 1) A process according to claim 1 in which the vinyl groups in the amount of polyvinyl aromatic coupling compound ranges from 2.0/1 to 4/1 vinyl groups per mole of active lithium catalyst employed. ### Claim 7 (depends on 4) A process according to claim 4 in which the molar ratio of the polar compound of (A) to the active lithium employed ranges from the mole ratio of 1/1 to 5/1. ### Claim 8 (depends on 5) A process according to claim 5 in which the molar ratio of the polar compound of (B) to active lithium catalyst employed ranges from about 4/1 to about 50/1. ### Claim 9 (depends on 1) A process according to claim 1 wherein the conjugated diolefin is butadiene or isoprene, the polystyryllithium catalyst is prepared from styrene or .alpha.-methylstyrene, the polar compound is glycol dimethyl ether or diethyl glycol dimethyl ether or N,N,N',N'-tetramethylethylenediamine and the polyvinyl aromatic coupling compound is divinylbenzene. ### Claim 10 (depends on 1) A process according to claim 1 in which the conjugated diolefin is butadiene or isoprene, the polystyryllithium is prepared from styrene or .alpha.-methylstyrene, the polar compound is tetrahydrofuran or 1,4-diazabicyclo-2.2.2-octane and the polyvinyl aromatic coupling compound is divinylbenzene.