# US 4,399,244 A · Glass fiber reinforced polyethylene terephthalate compositions having improved heat distortion temperatures

> Agents: this data is available as JSON from the patentgrep API and MCP server — see https://patentgrep.com/llms.txt

- Number: US 4,399,244 A
- Document ID: US4399244A
- Status: Granted
- Kind: A
- Application number: 06/095,276
- Filed: 1979-11-19
- Granted: 1983-08-16
- Earliest claimed: 1979-11-19
- Assignees: Bayer Aktiengesellschaft
- Inventors: Peter Bier
- Web page: https://patentgrep.com/patent/US4399244A

## CPC

- C08L 67/02: Polyesters derived from dicarboxylic acids and dihydroxy compounds (C08L67/06 takes precedence)
- C08L: COMPOSITIONS OF MACROMOLECULAR COMPOUNDS (compositions based on polymerisable monomers C08F, C08G; artificial filaments or fibres D01F; textile treating compositions D06)

## Abstract

This disclosure is concerned with glass reinforced polyethylene terephthalate compositions which have improved heat distortion temperatures when molded into cold molds due to the incorporation of an organic imide containing compound having a melting point in excess of 240.degree. C. These compositions have enhanced crystallization velocities which allows them to be molded into colder molds with faster cycle times than is conventional for polyethylene terephthalate compositions and still obtain crystalline parts with optimum properties including heat distortion temperatures. Mold temperatures of less than 120.degree. C. may be utilized without impairment of these properties.

## Claims

### Claim 1

A thermoplastic composition comprising:
(a) from 20 to 92% by weight of a polyethylene terephthalate having an intrinsic viscosity of at least 0.3 dl/g measured as a 0.5% by weight solution in a 1:1 mixture of phenol and tetrachloroethane at 25.degree. C.,
(b) from 5 to 60% by weight of glass fibers, and
(c) from 3 to 20% by weight of an organic compound containing at least one imide group and having a melting point greater than 240.degree. C.

### Claim 2 (depends on 1)

The composition of claim 1, wherein the organic imide containing compound is an N,N'-alkylene bis-(tetrahalophthalimide).

### Claim 3 (depends on 2)

The composition of claim 2, wherein
(a) the polyethylene terephthalate has an intrinsic viscosity of at least 0.5 dl/g,
(b) the glass fibers are present in 20 to 40% by weight, and
(c) the imide containing compound is present in 5 to 15% by weight.

### Claim 4

A thermoplastic molding composition comprising:
(a) from about 20 to 92% by weight of polyethylene terephthalate having an intrinsic viscosity of at least 0.3 dl/g measured as a 0.5% by weight solution in a 1:1 mixture of phenol and tetrachloroethane at 25.degree. C.,
(b) from 5 to 60% by weight of glass fibers, and
(c) from 3 to 20% by weight of an organic compound containing at least one phthalimide group and having a melting point greater than 240.degree. C.

### Claim 5 (depends on 4)

The composition of claim 4, wherein (a) polyethylene terephthalate, has an intrinsic viscosity of at least 0.5 dl/g, (b) glass fibers are present at 20-40% by weight, and (c) the phthalimide-containing compound is present in 5 to 15% by weight.

### Claim 6 (depends on 1)

The composition of claim 1, wherein the phthalimide-containing compound is an N,N'-alkylene bis-(tetrahalophthalimide).