Formation of packaging material
OwnerDonald E. Beckettinventor
Life of this patent
Estimating the term…
Abstract
A pattern is formed in rapid and continuous manner on aluminized polymer film by printing the aluminum surface with a sodium hydroxide-resistant material, which may be pigmented, contacting the non-overprinted areas of the aluminum with hot aqueous sodium hydroxide solution to dissolve the aluminum rapidly from the base polymeric film and leave unaffected the overprinted areas, and washing the spent sodium hydroxide solution from the film. The steps are carried on a continuous web of aluminized film and result in pattern of opaque areas and transparent areas, corresponding to the overprinted and non-overprinted areas of the film.
Claims8
A continuous method of forming a repetitive pattern on a roll of aluminized polymer film which comprises:
- (a) continuously feeding a web of said aluminized polymer film from said foll at a web speed of up to about 1000 ft/min;
- (b) printing said web with a pattern of etchant-resistant material corresponding to the pattern desired on the aluminized surface thereof;
- (c) applying aqueous sodium hydroxide solution having a concentration of up to about 25 wt % at a temperature of about 15.degree. to about 100.degree. C. across the whole width of the web to contact the pattern on the web;
- (d) allowing said sodium hydroxide solution to remain in contact with said web as it is conveyed for about 0.1 to about 10 seconds to permit said sodium hydroxide to dissolve aluminum only from areas of said web not having said pattern of etchant-resistant material applied thereto;
- (e) washing the spent sodium hydroxide solution from said web to leave said pattern of etchant-resistant material on a transparent polymeric film;
- and
- (f) drying the resulting washed web.
Dependencies are inferred from the claim text.