# US 4,398,967 A · Method for inhibiting alkali metal corrosion of nickel-containing alloys > Agents: this data is available as JSON from the patentgrep API and MCP server — see https://patentgrep.com/llms.txt - Number: US 4,398,967 A - Document ID: US4398967A - Status: Granted - Kind: A - Application number: 06/203,195 - Filed: 1980-11-03 - Granted: 1983-08-16 - Earliest claimed: 1979-09-11 - Inventors: Jackson H. DeVan; James E. Selle - Web page: https://patentgrep.com/patent/US4398967A ## CPC - C23F 11/00: Inhibiting corrosion of metallic material by applying inhibitors to the surface in danger of corrosion or adding them to the corrosive agent (adding inhibitors to mineral oil, fuels, or lubricants C10; adding inhibitors to pickling solutions C23G) - C23F: NON-MECHANICAL REMOVAL OF METALLIC MATERIAL FROM SURFACE (working metal by laser beams B23K26/00; desurfacing by applying flames B23K7/00; working of metal by electro-erosion B23H; producing decorative effects by removing surface material, e.g. by engraving, by etching, B44C1/22; electrolytic etching or polishing C25F); INHIBITING CORROSION OF METALLIC MATERIAL OR INCRUSTATION IN GENERAL; MULTI-STEP PROCESSES FOR SURFACE TREATMENT OF METALLIC MATERIAL INVOLVING AT LEAST ONE PROCESS PROVIDED FOR IN CLASS C23 AND AT LEAST ONE PROCESS COVERED BY SUBCLASS C21D OR C22F OR CLASS C25 ## Abstract Structural components of nickel-containing alloys within molten alkali metal systems are protected against corrosion during the course of service by dissolving therein sufficient aluminum, silicon, or manganese to cause the formation and maintenance of a corrosion-resistant intermetallic reaction layer created by the interaction of the molten metal, selected metal, and alloy. ## Claims ### Claim 1 In a closed apparatus consisting essentially of nickel-containing alloy components exposed to a molten alkali metal corrosive environment, the method of inhibiting corrosion by said molten alkali metal comprising dissolving in said molten alkali metal a metal selected from the group consisting of aluminum, silicon, and manganese in an amount sufficient to cause the formation of a corrosion-resistant coating on said exposed alloy components. ### Claim 2 (depends on 1) The method of claim 1 wherein subsequent additions of the selected metal are made as necessary to maintain said corrosion-resistant coating at a thickness sufficient to limit corrosion of said alloy during its service life. ### Claim 3 (depends on 1) The method of claim 1 wherein the amount of selected metal does not exceed its saturation concentration within the alkali metal, and is no more than 5 wt.% of the molten metal. ### Claim 4 (depends on 2) The method of claim 2 wherein subsequent additions of the selected metal are made as needed to maintain the selected metal concentration in excess of 0.1 wt.% of the alkali metal. ### Claim 5 In an operating apparatus consisting essentially of nickel-containing alloy components the process of inhibiting corrosion by a molten alkali metal in contact with the interior of said apparatus comprising initially dissolving within said molten metal a minor amount of a metal selected from the group consisting of aluminum, silicon, and manganese, and thereafter maintaining said selected metal at a concentration sufficient to limit corrosion of said components by said molten metal. ### Claim 6 (depends on 5) The process of claim 5 wherein said minor amount is less than the saturation level of said selected metal within the molten metal. ### Claim 7 (depends on 5) The process of claim 5 wherein the selected metal amount is in excess of 0.1 wt.% and less than 5 wt.% of the molten metal. ### Claim 8 In a closed operating system consisting essentially of nickel-containing alloy components exposed to a molten alkali metal, the process of inhibiting corrosion of said components comprising the formation and maintenance of an intermetallic reaction layer of nickel and a metal selected from the group consisting of aluminum, silicon, and manganese on said components, said layer being formed by dissolving a minor amount of the selected metal within a predominate amount of the molten metal and maintaining the concentration of said selected metal within said molten metal throughout the operating cycle of said system. ### Claim 9 In a closed apparatus functioning within its operating cycle, said closed apparatus defining at least one interior compartment consisting essentially of a nickel-containing alloy used for confining therein molten lithium under corrosive conditions, the process of inhibiting corrosion in said compartment by contacting and maintaining said contact during the operating cycle, the compartment with molten lithium having dissolved therein a metal selected from the group consisting of aluminum, silicon, and manganese for sufficient time and temperature to cause an interreaction between said nickel-containing alloy and metal to form a corrosion-resistant intermetallic reaction layer on the compartment surface exposed to lithium. ### Claim 10 (depends on 1) The method of claim 1 wherein the reaction layer is Ni-Al. ### Claim 11 (depends on 1) The method of claim 1 wherein the reaction layer is Ni-Si. ### Claim 12 (depends on 1) The method of claim 1 wherein the reaction layer is Ni-Mn. ### Claim 13 (depends on 2) The method of claim 2 wherein the apparatus is monitored by conventional techniques to determine whether subsequent additions should be made based on the remaining amount of selected metal dissolved within said alkali metal.