Energy storage element and method of making same
AssigneeArbed S.A.
InventorR. Schockmel
Life of this patent
Estimating the term…
Abstract
An energy-storage element, i.e. a body of high heat capacity capable of storing thermal energy and especially electrothermal energy, consists of 50-95% magnesium oxide, 5-50% iron oxide and a chemical binder, the mean particle size of the magnesium oxide lying between 0.1 and 4 mm and that of the iron oxide below 0.5 mm, preferably between 0.01 and 0.2 mm.
Claims9
A refractory heat-storage element for the storage of thermal energy consisting essentially of 50-95% magnesium oxide, 5-50% iron oxide, and a chemical binder, the mean particle size of the magnesium oxide being between 0.1 mm and 4 mm and the mean particle size of the iron oxide being less than 0.5 mm, wherein the magnesium oxide is in the form of comminuted used refractory brick having a particle size distribution of the Fuller-Bolomey type and containing more than 85% MgO.
A method of making a refractory body, for use as a heat-storage element, comprising the steps of blending 50-95% magnesium oxide, 5-50% iron oxide and a chemical binder to form a mass;
- pressing said mass at a pressure of substantially 1-3 t/cm.sup.2 to provide a body having the shape of said element;
- and heating said body for a period of about 3 hours at a temperature of about 250.degree. C., wherein said magnesium oxide is in the form of comminuted used magnesium oxide refractory brick containing iron oxide, and the quantity of iron oxide added to said blend is dimensioned to compensate for the iron oxide in the comminuted used bricks.
A method of making a refractory body for electro-thermal storage and release of heat, said method comprising the steps of:
- (a) comminuting used magnesium oxide furnace-lining brick containing iron oxide;
- (b) blending 50 to 95% of the comminuted used brick with 5 to 50% of iron oxide ore and adding iron sulfate to form a mixture consisting predominantly of MgO and the balance mostly of iron oxides;
- (c) pressing the mixture formed in step (b) at a pressure of substantially 1-3 t/cm.sup.2 to shape the same into the configuration of said body;
- and
- (d) heating the pressed shaped mixture for a period of about 3 hours at a temperature of about 250.degree. C.
Dependencies are inferred from the claim text.