# US 4,396,822 A · Welding wire for automatic arc welding > Agents: this data is available as JSON from the patentgrep API and MCP server — see https://patentgrep.com/llms.txt - Number: US 4,396,822 A - Document ID: US4396822A - Status: Granted - Kind: A - Application number: 06/312,138 - Filed: 1981-10-16 - Granted: 1983-08-02 - Earliest claimed: 1980-10-16 - Assignees: Nissan Motor Co., Ltd. - Inventors: Katsuhiro Kishida; Sumio Hirao; Hirohiko Date - Web page: https://patentgrep.com/patent/US4396822A ## CPC - B23K 35/0266: {flux-cored} - B23K 35/3066: {with Ni as next major constituent} - B23K: SOLDERING OR UNSOLDERING; WELDING; CLADDING OR PLATING BY SOLDERING OR WELDING; CUTTING BY APPLYING HEAT LOCALLY, e.g. FLAME CUTTING; WORKING BY LASER BEAM ## Abstract A welding wire for automatic arc welding, which is particularly suitable for use in build-up welding operation for the purpose of providing hard surface to a metal die. The welding wire consists of a continuous tubular metal casing and a core composition charged in the interior of the casing and comprises such amounts of Ni, Si, B, Nb and C as essential alloying elements that the deposited metal contains at least 40% of Ni, 3-8% of Si, 0.1-0.4% of B, 0.3-1.8% of Nb and 0.2-1.5% of C, all by weight. Preferably, either a practically pure Ni strip or an Fe-Ni alloy strip is used as the material of the casing, and the core composition in the form of a powder mixture contains necessary amounts of Ni, Si, B, Nb and C, optionally with the addition of a small amount of Zr. The deposited metal given by this welding wire has high wear resistance and good antifrictional property and seldom suffers from weld cracks. ## Claims ### Claim 1 A welding wire for automatic arc welding, the wire consisting of a continuous tubular metal casing and a core composition charged in the interior of the casing and comprising such amounts of Ni, Si, B, Nb and C as essential alloying elements that deposited metal given by the welding wire contains at least 40% by weight of Ni, 3 to 8% by weight of Si, 0.1 to 0.4% by weight of B, 0.3 to 1.8% by weight of Nb and 0.2 to 1.5% by weight of C. ### Claim 2 (depends on 1) A welding wire according to claim 1, wherein the balance of said deposited metal consists of Fe and inevitable impurities. ### Claim 3 (depends on 1) A welding wire according to claim 1, further comprising such an amount of Zr that said deposited metal contains up to 0.20% by weight of Zr. ### Claim 4 (depends on 3) A welding wire according to claim 3, wherein the balance of said deposited metal consists of Fe and inevitable impurities. ### Claim 5 (depends on 1) A welding wire according to claim 1, wherein the amount of Ni contained in the welding wire is at least 42% of the total weight of a unit length of the welding wire. ### Claim 6 (depends on 5) A welding wire according to claim 5, wherein the material of said casing contains at least 50% by weight of Ni. ### Claim 7 (depends on 6) A welding wire according to claim 6, wherein said core composition comprises Si, B, Nb and C respectively amounting to the following percentages of the total weight of a unit length of the welding wire: Si: 3.3 to 9.0%; B: 0.12 to 0.50%; Nb: 0.33 to 2.0% ; C: 0.3 to 2.0% ; ### Claim 8 (depends on 7) A welding wire according to claim 7, wherein said core composition further comprises Zr in an amount not larger than 0.3% of the total weight of a unit length of the welding wire. ### Claim 9 (depends on 6, 7) A welding wire according to claim 6 or 7, wherein said core composition further comprises Ni in an amount not smaller than 10% of the total weight of a unit length of the welding wire. ### Claim 10 (depends on 8) A welding wire according to claim 8, wherein the balance of said core composition consists of Fe and inevitable impurities. ### Claim 11 (depends on 10) A welding wire according to claim 10, wherein the material of said casing contains at least 95% by weight of Ni. ### Claim 12 (depends on 10) A welding wire according to claim 10, wherein the material of said casing consists essentially of 50 to 60% by weight of Ni and the balance of Fe. ### Claim 13 (depends on 7) A welding wire according to claim 7, wherein said core composition is in the form of a powder mixture. ### Claim 14 (depends on 7) A welding wire according to claim 7, wherein the ratio of the weight of said core composition to the total weight of a unit length of the welding wire is in the range from 20:100 to 45:100. ### Claim 15 (depends on 1) A welding wire according to claim 1, wherein said casing is formed of a metal strip rolled up cylindrically such that one of two opposite side edge regions of said strip laps over the other side edge region, said core composition being in the form of a powder mixture. ### Claim 16 (depends on 15) A welding wire according to claim 15, wherein the ratio of the weight of said core composition to the total weight of a unit length of the welding wire is in the range from 40:100 to 45:100. ### Claim 17 (depends on 1) A welding wire according to claim 1, wherein said casing is formed of a metal strip rolled up generally cylindrically such that two opposite side edge regions of said strip are brought into close contact with each other and folded inwardly so as to constitute a ridge which protruds into the interior of said casing and extends axially of said casing, said core composition being in the form of a powder mixture. ### Claim 18 (depends on 17) A welding wire according to claim 17, wherein the ratio of the weight of said core composition to the total weight of a unit length of the welding wire is in the range from 30:100 to 35:100. ### Claim 19 (depends on 17) A welding wire according to claim 17, wherein said strip is additionally folded inwardly in a region distant from both of said two side edge regions such that the additionally folded region constitutes another ridge which protrudes into the interior of said casing and extends axially of said casing. ### Claim 20 (depends on 19) A welding wire according to claim 19, wherein the ratio of the weight of said core composition to the total weight of a unit length of the welding wire is in the range from 20:100 to 25:100.