# US 4,396,437 A · Selective encapsulation, controlled atmosphere annealing for III-V semiconductor device fabrication

> Agents: this data is available as JSON from the patentgrep API and MCP server — see https://patentgrep.com/llms.txt

- Number: US 4,396,437 A
- Document ID: US4396437A
- Status: Granted
- Kind: A
- Application number: 06/260,455
- Filed: 1981-05-04
- Granted: 1983-08-02
- Earliest claimed: 1981-05-04
- Assignees: Hughes Aircraft Company
- Inventors: Siang P. Kwok; Milton Feng; Victor K. Eu
- Web page: https://patentgrep.com/patent/US4396437A

## CPC

- H10P 95/904: {of Group III-V semiconductors}
- H10P: GENERIC PROCESSES OR APPARATUS FOR THE MANUFACTURE OR TREATMENT OF DEVICES COVERED BY CLASS H10

## Abstract

A post-ion implantation annealing technique is provided to remove implantation damage in the active region of III-V (e.g., GaAs) semiconductor devices formed in a III-V semi-insulating substrate and separated by a field region. The technique involves applying a dielectric encapsulation selectively over the device active area and annealing in a controlled reducing atmosphere which includes the Group V element (e.g., arsenic). The dielectric encapsulant over the active region permits migration of the species employed to render the substrate semi-insulating (e.g., Cr in GaAs substrates), thereby resulting in high carrier mobility in the active region. Without encapsulation, migration of the species in the field region is substantially suppressed, thereby resulting in good inter-device isolation.

## Claims

### Claim 1

A process for fabricating III-V semiconductor devices having an active region formed on a III-V substrate rendered semi-insulating by a species, said process including at least one ion implantation step, wherein the improvement includes removing implantation damage by the following steps:
(a) forming a layer of dielectric material over said active region, said dielectric material capable of gettering of said species; and
(b) annealing the partially coated substrate in a reducing atmosphere including said Group V element at a temperature and for a time sufficient to substantially remove all implantation damage in said active region.

### Claim 2 (depends on 1)

The process of claim 1 in which said III-V substrate comprises GaAs and said species comprises Cr.

### Claim 3 (depends on 2)

The process of claim 2 in which said reducing atmosphere includes arsenic, whose partial pressure is effective to avoid depletion of Cr near the surface of said III-V substrate.

### Claim 4 (depends on 3)

The process of claim 3 in which said reducing atmosphere comprises a mixture of hydrogen and arsenic.

### Claim 5 (depends on 1)

The process of claim 1 in which said III-V substrate comprises InP and said species comprises Fe.

### Claim 6 (depends on 1)

The process of claim 1 in which said dielectric material is selected form the group consisting of SiO.sub.2, Si.sub.3 N.sub.4 and mixtures thereof.

### Claim 7 (depends on 6)

The process of claim 6 in which the thickness of said dielectric material ranges from about 50 to 3,000 A.

### Claim 8 (depends on 7)

The process of claim 7 in which said thickness ranges from about 1,000 to 2,000 A.

### Claim 9 (depends on 1)

The process of claim 1 in which said annealing is performed at a temperature between about 800.degree. and 900.degree. C. for about 20 to 40 minutes.