Pneumatic tire including a curable, storage-stable and solventless single component sealant composition
AssigneeThe Firestone Tire & Rubber Company
InventorsJames A. Davis, Russell W. Koch
Life of this patent
Estimating the term…
Abstract
A curable, storage-stable and solventless single component sealant for pneumatic tires having as its essential sealant functioning components a liquid low molecular weight hydroxy terminated polybutadiene diol, an antioxidant, a polymeric isocyanate, and, a polyurethane catalyst; this sealant can be blended with a sealant optimizing amount of a masterbatch.
Claims10
A pneumatic tire having a sealant functioning amount of a cured sealant composition contiguous to the inner surface of the inner liner of said tire, said sealant being a curable, storage-stable and solventless one-shot component sealant for pneumatic tires having as its essential sealant functioning components from about 60 to about 100 parts of a liquid low molecular weight hydroxy terminated polybutadiene diol, from about 1/2 to about 5 parts of an antioxidant, from about 4 to about 7 parts of an polymeric isocyanate, the ratio of NCO/OH being within the range of from about 0.65 to about 1.0, and, from about 0.5 to about 2.5 parts of a polyurethane catalyst blended with a sealant optimizing amount of a masterbatch having as its essential components:
- a. from about 100 to about 600 parts of a rubber process oil;
- b. from about 25 to about 200 parts of a low molecular weight rubber;
- c. from about 5 to about 50 parts of a tackifier;
- d. from about 1 to about 15 parts of a butyl rubber curing resin;
- e. from about 0.5 to about 5.0 parts of a nonvolatile antioxidant;
- and
- f. from about 5 to about 50 parts of finely ground bituminous coal dust.
A pneumatic tire having a sealant functioning amount of a cured sealant position contiguous to the inner surface of the inner liner of said tire, said sealant being a curable, storage-stable and solventless one-shot component sealant for pneumatic tires having as its essential sealant components about 80 parts of a liquid low molecular weight diol, about 0.8 part of an antioxidant, about 5.65 parts of a polymeric isocyanate, the ratio of NCO/OH being within the range of from about 0.65 to about 1.0, and, about 2 parts of a polyurethane catalyst blended with a sealant optimizing amount of a masterbatch having as its essential components:
- a. about 345 parts of a rubber process oil;
- b. about 115 parts of a low molecular weight rubber;
- c. about 20 parts of a tackifier;
- d. from about 2 to about 5 parts of a butyl rubber curing resin;
- e. about 2.5 parts of a nonvolatile antioxidant;
- and
- f. about 10 parts of finely ground bituminous coal dust.
A sealant composition for pneumatic tires comprising a blend of;
- (A) a curable, storage-stable and solventless one-shot component sealant for pneumatic tires having as its essential sealant functioning components from about 60 to about 100 parts of a liquid low molecular weight hydroxy-terminated polybutadiene diol, from about 0.5 to about 5 parts of an non-volatile antioxidant, from about 4 to about 7 parts of an polymeric isocyanate, the ratio of NCO/OH being within the range of from about 0.65 to about 1.0, and from about 0.5 to about 2.5 parts of a polyurethane catalyst;
- and
- (B) a sealant amount of a masterbatch having as its essential components:
- a. from about 100 to about 600 parts of a rubber process oil;
- b. from about 25 to about 200 parts of a low molecular weight rubber;
- c. from about 5 to about 50 parts of a tackifier;
- d. from about 1 to about 15 parts of a butyl rubber curing resin;
- e. from about 0.5 to about 5.0 parts of a non-volatile antioxidant;
- and
- f. from about 5 to about 50 parts of carbon black bituminous coal dust and mixtures thereof.
A sealant composition for pneumatic tires comprising a blend of;
- (A) a curable, storage-stable and solventless one-shot component sealant for pneumatic tires having as its essential sealant components about 80 parts of a liquid low molecular weight diol, about 0.8 parts of a non-volatile antioxidant, about 5.65 parts of a polymeric isocyanate, the ratio of NCO/OH being within the range of from about 0.65 to about 1.0, and about 2 parts of a polyurethane catalyst;
- and
- (B) a sealant amount of a masterbatch having as its essential components:
- a. about 345 parts of a rubber process oil;
- b. about 115 parts of a low molecular weight rubber;
- c. about 20 parts of a tackifier;
- d. from about 2 to about 5 parts of a butyl rubber curing resin;
- e. about 2.5 parts of a nonvolatile antioxidant;
- and
- f. about 10 parts of carbon black bituminous coal dust and mixtures thereof.
Dependencies are inferred from the claim text.