# US 4,395,539 A · Amorphous aromatic polyester modified with amine and UV curable composition containing the same

> Agents: this data is available as JSON from the patentgrep API and MCP server — see https://patentgrep.com/llms.txt

- Number: US 4,395,539 A
- Document ID: US4395539A
- Status: Granted
- Kind: A
- Application number: 06/401,756
- Filed: 1982-07-26
- Granted: 1983-07-26
- Earliest claimed: 1981-08-06
- Assignees: Eastman Kodak Company
- Inventors: James G. Pacifici; Gordon C. Newland; Howard G. Moore
- Web page: https://patentgrep.com/patent/US4395539A

## CPC

- G03F 7/032: with binders
- C08F 299/0435: {with sensitising agents}
- C08G 63/6856: {Dicarboxylic acids and dihydroxy compounds}
- G03F: PHOTOMECHANICAL PRODUCTION OF TEXTURED OR PATTERNED SURFACES, e.g. FOR PRINTING, FOR PROCESSING OF SEMICONDUCTOR DEVICES; MATERIALS THEREFOR; ORIGINALS THEREFOR; APPARATUS SPECIALLY ADAPTED THEREFOR; (phototypographic composing devices B41B; photosensitive materials or processes for photographic purposes G03C; electrophotography, sensitive layers or processes therefor G03G)
- C08F: MACROMOLECULAR COMPOUNDS OBTAINED BY REACTIONS ONLY INVOLVING CARBON-TO-CARBON UNSATURATED BONDS
- C08G: MACROMOLECULAR COMPOUNDS OBTAINED OTHERWISE THAN BY REACTIONS ONLY INVOLVING UNSATURATED CARBON-TO-CARBON BONDS

## Abstract

The present invention provides a novel linear amorphous aromatic polyester comprising units derived from (i) terephthalic acid, (ii) 1,2-propanediol or mixtures of 1,2-propanediol with up to 20 mole percent of ethylene glycol, based upon the total of 1,2-propanediol and ethylene glycol, and (iii) about 5 to 30 mole percent, based upon the total of (i), (ii), and (iii), of a glycol which contains a tertiary amine group, the amine containing glycol having a specified structure and the polyester having an inherent viscosity of about 0.05 to 0.5 dl/g when measured in 60:40 phenol:tetrachloroethane at a concentration of 0.5 g/100 ml at 25.degree. C. The novel polyester is useful as a crosslinking resin and as a photoinitiator for UV curable coating and ink compositions. Also provided is a specified ultraviolet radiation curable coating composition. The composition comprises a mixture of A. about 4.5 to 49.5% by weight of the novel amine-modified polyester described above; B. about 50 to 95 percent by weight of a photopolymerizable or photocrosslinkable ethylenically unsaturated compound; and C. about 0.5 to 25 percent by weight of a photoinitiator. The photoinitiator is selected from the group consisting of benzil, lower alkyl substituted benzil, benzoin ethers, haloalkyl ketones, aromatic ketones, lower alkyl substituted aromatic ketones, aromatic ketones in combination with amines, and mixtures thereof. The ethylenically unsaturated compound is most preferably selected from the group consisting of glycidyl acrylate, glycidyl methacrylate, methyl acrylate, methyl methacrylate, ethyl acrylate, ethyl methacrylate, and mixtures thereof. The coating composition provided by the present invention gives clear insoluble coatings which are useful as protective and/or decorative coatings.

## Claims

### Claim 1

A novel linear amorphous aromatic polyester comprising units derived from (i) terephthalic acid, (ii) 1,2-propanediol or mixtures of 1,2-propanediol with up to 20 mole percent of ethylene glycol, based upon the total of 1,2-propanediol and ethylene glycol, and (iii) about 5 to 30 mole percent, based upon the total of (i), (ii), and (iii), of a glycol which contains a tertiary amine group, said glycol having the general formula ##STR14## where n is an integer within the range of 1 to 20 and each of x and y is independently an integer within the range of 1 to 30 with the sum of x+y being less than or equal to 60,
or the general formula ##STR15## where each of p and q is independently 0 or a positive integer not greater than 10, and where R.sub.1 and R.sub.2 are lower alkyl groups and can be the same or different and R.sub.3 is a lower alkyl group or a group of the formula ##STR16## said polyester having an inherent viscosity of about 0.05 to 0.5 dl/g when measured in 60:40 phenol:tetrachlorothane at a concentration of 0.5 g/100 ml at 25.degree. C.

### Claim 2 (depends on 1)

The polyester of claim 1 wherein said polyester exhibits an inherent viscosity of about 0.1 to 0.5 dl/g when measured at a concentration of 0.5 g/100 ml in 60:40 phenol:tetrachloroethane at 25.degree. C.