# US 4,395,510 A · Novel olefin polymer compositions and foamed articles prepared therefrom having improved elevated temperature dimensional stability

> Agents: this data is available as JSON from the patentgrep API and MCP server — see https://patentgrep.com/llms.txt

- Number: US 4,395,510 A
- Document ID: US4395510A
- Status: Granted
- Kind: A
- Application number: 06/422,768
- Filed: 1982-09-24
- Granted: 1983-07-26
- Earliest claimed: 1980-05-29
- Assignees: The Dow Chemical Company
- Inventors: Chung P. Park
- Web page: https://patentgrep.com/patent/US4395510A

## CPC

- C08J 9/0028: {containing nitrogen}
- C08K 5/20: Carboxylic acid amides
- C08J 2323/02: not modified by chemical after treatment
- C08J: WORKING-UP; GENERAL PROCESSES OF COMPOUNDING; AFTER-TREATMENT NOT COVERED BY SUBCLASSES C08B, C08C, C08F, C08G or C08H (working, e.g. shaping, of plastics B29)
- C08K: Use of inorganic or non-macromolecular organic substances as compounding ingredients (paints, inks, varnishes, dyes, polishes, adhesives C09)

## Abstract

Elevated temperature distortion characteristics of freshly prepared olefin polymer foams are substantially improved by employing in the preparation thereof a small amount (e.g., from about 0.15 to about 10 weight percent based on the olefin polymer) of certain selected N-substituted fatty acid amide compounds of the formula: ##STR1## wherein R.sub.1 represents an alkyl group of from 11 to 17 carbon atoms and R.sub.2 represents an alkyl group of from 12 to 18 carbon atoms.

## Claims

### Claim 1

An olefin polymer composition consisting essentially of an olefin polymer and from about 0.15 to about 10 weight percent based upon the weight of said olefin polymer of an N-substituted fatty acid amide of the Formula: ##STR4## wherein R.sub.1 represents an alkyl group of from about 11 to about 17 carbon atoms and R.sub.2 represents an alkyl group of from about 12 to about 18 carbon atoms, said N-substituted fatty acid amide being selected from the group consisting of N-lauryl lauric acid amide, N-lauryl myristamide, N-myristyl myristamide, N-palmityl myristamide, N-lauryl palmitamide, N-myristyl palmitamide, N-palmityl palmitamide, N-palmityl stearamide and N-stearyl stearamide; said N-substituted fatty acid amide being employed in an amount such that if said olefin polymer composition is foamed by extrusion using a volatile organic blowing agent, the presence of said fatty acid amide prevents the freshly prepared foam from shrinking by more than 10% from its initially foamed volume when subjected to prolonged exposure to atmospheric pressure air at 150.degree. F.

### Claim 2 (depends on 1)

The olefin polymer composition of claim 1 wherein the olefin polymer is polyethylene, an ethylene-vinyl acetate copolymer or an ethylene-acrylic acid copolymer.

### Claim 3 (depends on 1)

The olefin polymer composition of claim 1 wherein the N-substituted fatty acid amide is N-stearyl stearamide, N-palmityl stearamide or N-palmityl palmitamide.

### Claim 4 (depends on 1)

The olefin polymer composition of claim 1 wherein the N-substituted fatty acid amide is selected from the group consisting of N-lauryl myristamide, N-myristyl myristamide, N-palmityl myristamide, N-myristyl palmitamide, N-palmityl palmitamide, N-palmityl stearamide and N-stearyl stearamide.

### Claim 5 (depends on 1)

The olefin polymer composition of claim 1 wherein the N-substituted fatty acid amide is employed in an amount sufficient to prevent a freshly prepared foam made from such composition using a volatile organic blowing agent from shrinking by more than 10 percent from its initial foamed volume when subjected to prolonged exposure to atmospheric pressure air at 150.degree. F.

### Claim 6 (depends on 1)

The olefin polymer composition of claim 1 which further comprises an auxiliary stability control agent selected from the group consisting of (a) higher alkyl amines, (b) fatty acid esters and (c) fatty acid amides different from those of Formula I above and wherein the combined weight of such auxiliary stability control agent and the Formula I compound is no more than about 10 weight percent based upon the weight of the olefin polymer.

### Claim 7 (depends on 6)

The olefin polymer composition of claim 6 wherein the auxiliary stability control agent is stearamide.

### Claim 8 (depends on 7)

The olefin polymer composition of claim 7 wherein the N-substituted fatty acid amide is employed in an amount ranging from about 0.2 to about 2 weight percent based upon the weight of the olefin polymer.

### Claim 9 (depends on 1)

The olefin polymer composition of claim 1 wherein the N-substituted fatty acid amide is employed in an amount of from about 0.7 to about 5 weight percent based upon the olefin polymer.