# US 4,394,479 A · Vinyl acetate interpolymer latices > Agents: this data is available as JSON from the patentgrep API and MCP server — see https://patentgrep.com/llms.txt - Number: US 4,394,479 A - Document ID: US4394479A - Status: Granted - Kind: A - Application number: 06/218,994 - Filed: 1980-12-22 - Granted: 1983-07-19 - Earliest claimed: 1980-12-22 - Assignees: Monsanto Company - Inventors: Irving Serlin - Web page: https://patentgrep.com/patent/US4394479A ## CPC - G03G 5/0217: {Inorganic components} - C08F 8/44: Preparation of metal salts or ammonium salts - G03G 5/0208: {obtained by reactions only involving carbon-to-carbon unsatured bonds} - G03G: ELECTROGRAPHY; ELECTROPHOTOGRAPHY; MAGNETOGRAPHY - C08F: MACROMOLECULAR COMPOUNDS OBTAINED BY REACTIONS ONLY INVOLVING CARBON-TO-CARBON UNSATURATED BONDS ## Abstract An aqueous latex consisting essentially of an acid modified vinyl ester interpolymer and 0.8 parts by weight or less of a protective colloid per 100 parts by weight of interpolymer. The vinyl ester interpolymer comprises about 3 to about 7 weight percent of carboxylic acid groups supplied by an interpolymerized C.sub.4 -C.sub.10 vinylene monobasic carboxylic acid monomer. The aqueous latex is useful as an aqueous dielectric coating binder in the manufacture of electrographic recording materials. ## Claims ### Claim 1 An aqueous latex consisting essentially of a partially neutralized acid-modified interpolymer of a C.sub.4 -D.sub.6 vinyl ester and a protective colloid, wherein the vinyl ester interpolymer comprises from about 3 to about 7 weight percent of carboxylic acid groups supplied by an interpolymerized C.sub.4 -C.sub.10 vinylene monobasic carboxylic acid monomer, wherein the neutralizing agent is a volatile base, wherein the concentration of protective colloid is less than about 0.8 parts by weight per 100 parts by weight of the interpolymer and wherein the particle size of the latex is in the range of from 0.05 to about 0.5 microns. ### Claim 2 (depends on 1) The aqueous latex according to claim 1 wherein the protective colloid is a polyvinyl alcohol comprising from about 10 to about 30 weight percent of unhydrolyzed polyvinyl acetate. ### Claim 3 (depends on 2) The aqueous latex according to claim 2, wherein the polyvinyl alcohol has a weight average molecular weight of at least about 80,000. ### Claim 4 (depends on 1, 2, 3) The aqueous latex according to claim 1, 2 or 3 wherein the vinyl ester is vinyl acetate. ### Claim 5 (depends on 4) The aqueous latex according to claim 4 wherein the vinylene monobasic carboxylic acid monomer is selected from the group consisting of crotonic acid, isocrotonic acid and methyl hydrogen maleate. ### Claim 6 (depends on 1, 2, 3) The aqueous latex according to claim 1, 2 or 3 wherein the volatile base is ammonia. ### Claim 7 (depends on 6) The aqueous latex according to claim 6 wherein the ammonia is from about 0.6 to about 0.80 equivalent of the interpolymerized acid monomer. ### Claim 8 (depends on 5) The aqueous latex according to claim 5 wherein the volatile base is ammonia and is from about 0.6 to about 0.80 equivalent of the interpolymerized acid. ### Claim 9 (depends on 1, 2, 3) The aqueous latex according to claim 1, 2 or 3 wherein the solids content is at least about 25% and the viscosity at 25.degree. C. is less than about 50,000 cps. ### Claim 10 (depends on 9) The aqueous latex according to claim 9 wherein the weight average molecular weight of the interpolymer is less than about 50,000. ### Claim 11 (depends on 8) The aqueous latex according to claim 8 wherein the solids content is at least about 25%, the viscosity at 25.degree. C. is less than about 50,000 cps and the weight average molecular weight of the interpolymer is less than about 50,000. ### Claim 12 A method of preparing an aqueous latex consisting essentially of a partially neutralized acid-modified interpolymer of a C.sub.4 -C.sub.6 vinyl ester and a protective colloid, wherein the vinyl ester interpolymer comprises from about 3 to about 7 weight percent of carboxylic acid groups supplied by an interpolymerized C.sub.4 -C.sub.10 vinylene monobasic carboxylic acid monomer, wherein the neutralizing agent is a volatile base, wherein the concentration of protective colloid is less than about 0.8 parts by weight per 100 parts by weight of the interpolymer and wherein the particle size of the latex is in the range of about 0.05 to about 0.5 microns, said method comprising: A. interpolymerizing the vinyl ester and vinylene monobasic carboxylic acid monomer in aqueous suspension at a pH in the range of about 6.0 to about 6.2 in the presence of the protective colloid while adding incrementally sufficient of the volatile base to neutralize from about 10 to about 30 percent of the vinylene monobasic carboxylic acid monomer; and B. adjusting the pH of the interpolymer suspension to a value in the range of about 6.2 to about 7.5 and agitating the interpolymer suspension to form the latex. ### Claim 13 (depends on 12) The method according to claim 12 wherein the volatile base is ammonia. ### Claim 14 (depends on 13) The method according to claim 13 wherein the protective colloid is a polyvinyl alcohol of weight average molecular weight at least about 80,000, comprising from about 10 to about 30 weight percent unhydrolyzed poly(vinyl acetate). ### Claim 15 (depends on 14) The method according to claim 14 wherein the vinyl ester is vinyl acetate and the vinylene monocarboxylic acid monomer is selected from the group consisting of crotonic acid, isocrotonic acid and methyl hydrogen maleate. ### Claim 16 (depends on 15) The method according to claim 15 wherein the solids content of the latex is at least about 25%, the viscosity at 25.degree. C. is less than about 50,000 cps and the weight average molecular weight of the interpolymer is less than about 50,000. ### Claim 17 (depends on 1, 2, 3) An aqueous coating composition comprising an intimate blend of the latex according to claim 1, 2 or 3 and up to about 500 parts by weight of an inert finely divided pigment per 100 parts by weight of interpolymer. ### Claim 18 (depends on 10) An aqueous coating composition comprising an intimate blend of the latex according to claim 10 and up to about 500 parts by weight of an inert finely divided pigment per 100 parts by weight of interpolymer. ### Claim 19 (depends on 11) An aqueous coating composition comprising an intimate blend of the latex according to claim 11 and up to about 500 parts by weight of an inert finely divided pigment per 100 parts by weight of interpolymer. ### Claim 20 (depends on 12) An aqueous coating composition comprising an intimate blend of the interpolymer latex prepared by the method of claim 12 and up to about 500 parts by weight of an inert finely divided pigment per 100 parts by weight of interpolymer.