# US 4,394,414 A · Aqueous sizing composition for glass fibers for use on chopped glass fibers > Agents: this data is available as JSON from the patentgrep API and MCP server — see https://patentgrep.com/llms.txt - Number: US 4,394,414 A - Document ID: US4394414A - Status: Granted - Kind: A - Application number: 06/268,541 - Filed: 1981-05-29 - Granted: 1983-07-19 - Earliest claimed: 1981-05-29 - Assignees: PPG Industries, Inc. - Inventors: Daniel G. Brown; Donald L. Motsinger - Web page: https://patentgrep.com/patent/US4394414A ## CPC - D21H 13/40: vitreous, e.g. mineral wool, glass fibres - C03C 25/26: Macromolecular compounds or prepolymers - C08K 5/16: Nitrogen-containing compounds {(C08K5/0091 takes precedence)} - Y10T 428/2962: Silane, silicone or siloxane in coating - Y10T 428/2964: Artificial fiber or filament - Y10T 442/604: Strand or fiber material is glass - D21H: PULP COMPOSITIONS; PREPARATION THEREOF NOT COVERED BY SUBCLASSES D21C OR D21D; IMPREGNATING OR COATING OF PAPER; TREATMENT OF FINISHED PAPER NOT COVERED BY CLASS B31 OR SUBCLASS D21G; PAPER NOT OTHERWISE PROVIDED FOR - C03C: CHEMICAL COMPOSITION OF GLASSES, GLAZES OR VITREOUS ENAMELS; SURFACE TREATMENT OF GLASS; SURFACE TREATMENT OF FIBRES OR FILAMENTS MADE FROM GLASS, MINERALS OR SLAGS; JOINING GLASS TO GLASS OR OTHER MATERIALS - C08K: Use of inorganic or non-macromolecular organic substances as compounding ingredients (paints, inks, varnishes, dyes, polishes, adhesives C09) - Y10T: TECHNICAL SUBJECTS COVERED BY FORMER US CLASSIFICATION ## Abstract An aqueous sizing composition having a cationic lubricant, amide compound, and cationic silicone polymer aqueous emulsion which is used to produce wet chopped sized glass fiber strands or which also has a film former to produce continuous glass fiber strands. The moisture content of the wet chopped glass fiber strands is controlled to within about 9 to about 20 weight percent. The sized wet chopped glass fiber strands have good flowability and when used to produce non-woven glass fiber strand mat, produces mat with good flexibility and tensile strength. ## Claims ### Claim 1 An aqueous sizing composition for glass fibers, comprising: a. one or more cationic lubricants, b. water soluble or dispersible amide selected from the group consisting of monoamides, diamides, melamine, diamides of saturated dicarboxylic acids, carbamides, non-polymeric amine-containing amides and mixtures thereof, c. curable silicone polymer in a cationic aqueous emulsion; and d. water in an amount to give a solids content in the range of about 0.1 to about 5 weight percent wherein the major amount of the solids of the sizing composition is comprised of cationic lubricant and emulsion. ### Claim 2 (depends on 1) Glass fiber strand formed by the wet chop glass fiber forming process having the dried residue of the sizing composition of claim 1. ### Claim 3 (depends on 1) Aqueous sizing composition of claim 1 wherein the cationic, curable, silicone polymer emulsion has the infrared spectrum of FIG. 1. ### Claim 4 (depends on 1) Aqueous sizing composition of claim 1 wherein the cationic lubricant is present in an amount in the range of about 0.2 to 3 weight percent. ### Claim 5 (depends on 1) An aqueous sizing composition of claim 1 wherein the water soluble or dispersible amide is present in an amount in the range of about 0.2 to 2 weight percent. ### Claim 6 (depends on 1) Aqueous sizing composition of claim 1 wherein the cationic, curable silicone polymer aqueous emulsion is present in an amount in the range of about 0.1 to about 1 weight percent. ### Claim 7 (depends on 1) Aqueous sizing composition of claim 1 wherein the cationic lubricant is an alkyl imidazoline reaction product of a tetraethylene pentamine and stearic acid. ### Claim 8 (depends on 1) Aqueous sizing composition of claim 1 wherein the water soluble or dispersible amide is urea. ### Claim 9 (depends on 1) Aqueous sizing composition of claim 1 wherein the cationic, curable silicone polymer in aqueous emulsion is an amine functional silicone polymer in an aqueous emulsion. ### Claim 10 (depends on 2) An aqueous solution for producing non-woven glass fiber strand mat comprising about 0.5 to 1 weight percent of the glass fiber strands of claim 2 wherein the lengths of the glass fiber strands vary from 1/4 inch to 3 inches and a filament diameter in the range of 3 to 27 microns. ### Claim 11 (depends on 10) Aqueous solution of claim 10 which also includes dispersing aids. ### Claim 12 (depends on 11) Aqueous solution of claim 11 wherein the dispersing aids are selected from polyoxyethylated tallow amine and a thickening agent. ### Claim 13 (depends on 11) Aqueous solution of claim 11 wherein the dispersing aid is a blend of alkyl sulfate quaternary of an alkyl amino fatty acid amine or amide in a water dispersible, liquid, mineral oil with an inorganic silica defoaming agent wherein the amount of the quaternary material is in the range of about 50 to about 95 weight percent of the blend and the amount of defoaming agent is around 5 to about 50 weight percent of the blend and water. ### Claim 14 (depends on 10) Non-woven glass fiber strand mat made from the aqueous solution of claim 10. ### Claim 15 (depends on 9) Aqueous sizing composition of claim 9, wherein the silicone polymer with amine groups is present in a cationic water emulsion. ### Claim 16 (depends on 1) Aqueous sizing composition of claim 1, wherein the cationic, curable silicone polymer has carboxyl groups. ### Claim 17 (depends on 1) Aqueous sizing composition of claim 1, wherein the cationic, curable silicone polymer has mercapto groups. ### Claim 18 (depends on 1) Aqueous sizing composition of claim 1, wherein the cationic, curable silicone polymer has acrylate or methacrylate groups. ### Claim 19 (depends on 1) Aqueous sizing composition of claim 1, which has present one or more silane coupling agents. ### Claim 20 (depends on 19) Aqueous sizing composition of claim 19, wherein the one or more silane coupling agents are selected from the group consisting of vinyl tris (2-methoxysilane) lubricant modified gamma-aminopropyltriethoxy silane and gamma-glycidoxypropyltrimethoxy silane. ### Claim 21 (depends on 14) Non-woven glass fiber mat of claim 14, in contact with a polymeric binder selected from the group consisting of urea formaldehyde, anionic urea formaldehyde, and cationic urea formaldehyde.