# US 4,394,334 A · Process and apparatus for deburring moulded parts produced by pressing > Agents: this data is available as JSON from the patentgrep API and MCP server — see https://patentgrep.com/llms.txt - Number: US 4,394,334 A - Document ID: US4394334A - Status: Granted - Kind: A - Application number: 06/341,643 - Filed: 1982-01-22 - Granted: 1983-07-19 - Earliest claimed: 1981-01-22 - Assignees: Lignotock Verfahrenstechnik GmbH - Inventors: Gunter H. Kiss - Web page: https://patentgrep.com/patent/US4394334A ## CPC - B27N 3/20: characterised by using platen-presses - B23D 79/005: {for thermal deburring (B23D79/025 takes precedence)} - B29C 33/40: Plastics, e.g. foam or rubber - B27N: MANUFACTURE BY DRY PROCESSES OF ARTICLES, WITH OR WITHOUT ORGANIC BINDING AGENTS, MADE FROM PARTICLES OR FIBRES CONSISTING OF WOOD OR OTHER LIGNOCELLULOSIC OR LIKE ORGANIC MATERIAL (containing cementitious material B28B; shaping of substances in a plastic state B29C; fibreboards made from fibrous suspensions D21J; drying F26B17/00) - B23D: PLANING; SLOTTING; SHEARING; BROACHING; SAWING; FILING; SCRAPING; LIKE OPERATIONS FOR WORKING METAL BY REMOVING MATERIAL, NOT OTHERWISE PROVIDED FOR (making toothed gears or the like B23F; cutting metal by applying heat locally B23K; arrangements for copying or controlling B23Q) - B29C: SHAPING OR JOINING OF PLASTICS; SHAPING OF MATERIAL IN A PLASTIC STATE, NOT OTHERWISE PROVIDED FOR; AFTER-TREATMENT OF THE SHAPED PRODUCTS, e.g. REPAIRING (making preforms B29B11/00; making laminated products by combining previously unconnected layers which become one product whose layers will remain together B32B37/00 - B32B41/00) ## Abstract A process and the apparatus for deburring moulded parts produced by pressing especially moulded parts of lignocellulose fibre mats. A small circumferential zone of the fibre mat between the edge contour of the moulded part to be deburred and the edge of the waste shoulder is thermically decomposed during pressing. The thermically decomposed material portion of the fibre mat is removed from the edge contour of the moulded part while taking off the moulded part from the press tools. The decomposition zone is limited by a circumferential groove shaped chamber provided in one of the press tools. The portion of the fibre mat enclosed in the chamber is practically uncompressed and the chamber is provided with different methods for the thermal decomposition. The decomposition methods cause a carbonization of the material in the decomposition zone which facilitates the removing of the waste shoulder from the moulded part so that an additional treatment by hand is unnecessary. ## Claims ### Claim 1 A process for deburring moulded parts produced by pressing large edge contours of poor heat-conducting materials formed of crushed, glued, organic, raw materials comprising the steps of: thermically decomposing the material of a small circumferential zone between the edge contour of the moulded part to be deburred and the waste shoulder during pressing of the moulded part; and removing the decomposed material from the edge contour when the moulded part is removed from the press tools. ### Claim 2 (depends on 1) The process according to claim 1, characterized in that the material of the fibre mat in the decomposition zone is compressed less than the material of the moulded part and of the waste shoulder. ### Claim 3 (depends on 1, 2) The process according to claims 1 or 2, characterized in that the heat necessary for the thermal decomposition is conducted through heat leading surfaces to the material of the decomposition zone. ### Claim 4 (depends on 1, 2, 3) The process according to one of the claims 1, 2 or 3, characterized in that the thermal decomposition is carried out by electrical resistance heating. ### Claim 5 (depends on 1, 2, 3) The process according to claims 1, 2 or 3, characterized in that the thermal decomposition is carried out by igniting a combustible gas mixture with a surplus of oxygen. ### Claim 6 (depends on 1, 2, 3) The process according to claims 1, 2 or 3, characterized in that the thermal decomposition is carried out in an oxygen atmosphere heating up to ignition temperature the material portion to be decomposed at one or more spots. ### Claim 7 (depends on 1, 2, 3, 4, 5, 6) The process according to claims 1, 2, 3, 4, 5 or 6, characterized in that the thermal decomposition is finished by introducing inert gas and/or a liquid into the decomposition zone. ### Claim 8 (depends on 1) The process according to claim 1 further including the steps of: providing an upper and a lower press tool; forming a circumferential groove shaped chamber in the lower press tool; forming a dipped edge protruding from the bottom surface of the edge contour of the moulded part in the upper press tool adjacent to the circumferential groove shaped chamber in the lower press tool to limit the decomposition zone, the dipping edge being closed by the upper press tool; constructing the wall of the chamber opposite to the dipping edge as a squeezing edge which serves as a heat conducting nose; and providing the chamber with a thermal decomposition means. ### Claim 9 (depends on 8) The process according to claim 8 characterized in that the volume of the chamber is larger than the volume of the uncompressed portion of the fibre mat to be decomposed and closed by the chamber. ### Claim 10 (depends on 8, 9) The process according to claims 8 or 9 characterized in that the chamber includes a heating wire contacting the fibre mat. ### Claim 11 (depends on 8, 9, 10) The process according to claims 8, 9 or 10 further including the step of: providing a supply lead for a combustible gas mixture and/or oxygen and an ignition for igniting the mixture and/or the oxygen. ### Claim 12 (depends on 8, 9, 10, 11) The process of according to claims 8, 9, 10 or 11 further including the step of: providing a supply lead which serves to introduce a medium into the chamber for finishing the decomposition process.