# US 4,393,563 A · Cold forced sintered powder metal annular bearing ring blanks

> Agents: this data is available as JSON from the patentgrep API and MCP server — see https://patentgrep.com/llms.txt

- Number: US 4,393,563 A
- Document ID: US4393563A
- Status: Granted
- Kind: A
- Application number: 06/266,931
- Filed: 1981-05-26
- Granted: 1983-07-19
- Earliest claimed: 1981-05-26
- Inventors: David T. Smith
- Web page: https://patentgrep.com/patent/US4393563A

## CPC

- C22C 33/0207: {Using a mixture of pre-alloyed powders or a master alloy}
- B22F 3/16: in successive or repeated steps
- F16C 33/64: Special methods of manufacture
- Y10T 29/49689: Race making
- C22C: ALLOYS (treatment of alloys C21D, C22F)
- B22F: WORKING METALLIC POWDER; MANUFACTURE OF ARTICLES FROM METALLIC POWDER; MAKING METALLIC POWDER (making alloys by powder metallurgy C22C); APPARATUS OR DEVICES SPECIALLY ADAPTED FOR METALLIC POWDER
- F16C: SHAFTS; FLEXIBLE SHAFTS; ELEMENTS OR CRANKSHAFT MECHANISMS; ROTARY BODIES OTHER THAN GEARING ELEMENTS; BEARINGS
- Y10T: TECHNICAL SUBJECTS COVERED BY FORMER US CLASSIFICATION

## Abstract

A method and material for the manufacture of improved bearing elements such as annular inner and outer bearing ring blanks for ball, roller and needle bearing assemblies comprising the steps of mixing a powder consisting substantially of iron with ferro-alloy powders of substantially smaller size, each ferro-alloy containing at least 80% iron and the balance being an alloying element, together with graphite powder and a lubricant, compacting the resulting mixture to form a preform, pre-sintering the preform, and then coating the sintered preform with a stop-off and lubricant. The preform is subjected to a plastic deformation of at least 50% in a cold (room temperature) forging operation to produce an article which is at least 98% dense and has approximately the shape of the finished article. This cold forged shape is resintered and annealed, after which the annealed and resintered shape is roll formed into substantially final dimensions. The article can be followed by a suitable heat treatment for hardening the shape.

## Claims

### Claim 1

A method for the manufacture of improved bearing elements, without high temperature forming which comprises the following steps:
(1) combining (a) powders consisting substantially of iron with (b) ferro-alloy powders each containing a maximum of 80% by weight iron and the balance of each alloying powder being either manganese, nickel, chromium, molybdenum, or vanadium, (c) graphite powder, and (d) a lubricant,
(2) mixing the resulting combination,
(3) compacting the resulting mixture to produce a preform,
(4) pre-sintering the preform,
(5) coating the sintered preform with a stop-off coating and lubricant,
(6) cold forging the coated and lubricated preform to achieve a plastic deformation of at least 50%, through a combination of lateral and vertical flow and produce an article being at least 98% dense and approximating the shape of the finished article,
(7) resintering the cold forged shape,
(8) annealing the resintered shape, and
(9) roll forming the annealed and resintered shape into substantially final dimensions.

### Claim 2 (depends on 1)

A method according to claim 1 in which:
said ferro-alloy powders have an average particle size smaller than the average particle size of said iron powder.

### Claim 3 (depends on 1)

A method according to claim 1 in which:
said ferro-alloy powders contain up to 95% by weight iron.

### Claim 4 (depends on 1)

A method according to claim 1 in which:
said ferro-alloy powders have a particle size below 200 mesh (74 micron).

### Claim 5 (depends on 1)

A method according to claim 1 in which:
said roll forming step (9) is followed by a heat treatment for hardening the shape.

### Claim 6 (depends on 5)

A method according to claim 5 in which:
said heat treatment consists of a through hardening treatment.

### Claim 7 (depends on 5)

A method according to claim 5 in which:
said heat treatment consists of a carburizing treatment.

### Claim 8 (depends on 1)

A method according to claim 1 in which:
said cold forging step (6) is carried out at a pressure of from 110 to 130 tons/sq. in. (1517 to 1793 MPa).

### Claim 9 (depends on 1)

A method according to claim 1 in which:
said compacting step (3) is carried out at a pressure of from 40 to 60 tons/sq. in. (552 to 827 MPa).

### Claim 10 (depends on 1)

A method according to claim 1 in which:
said shape is parted into several pieces between annealing step (8) and roll forming step (9).

### Claim 11 (depends on 1)

A method according to claim 1 in which said bearing element is an inner or outer ring for a ball bearing assembly.

### Claim 12 (depends on 1)

A method according to claim 1 in which said bearing element is a needle bearing ring or cup.

### Claim 13 (depends on 1)

A method according to claim 1 in which said bearing element is an inner or outer ring for a roller bearing assembly.