# US 4,391,961 A · Process for preparing light colored petroleum resins and resins produced thereby (CS-203)

> Agents: this data is available as JSON from the patentgrep API and MCP server — see https://patentgrep.com/llms.txt

- Number: US 4,391,961 A
- Document ID: US4391961A
- Status: Granted
- Kind: A
- Application number: 06/252,434
- Filed: 1981-04-09
- Granted: 1983-07-05
- Earliest claimed: 1981-04-09
- Assignees: Exxon Research & Engineering Co.
- Inventors: Augustus B. Small; Vincent L. Hughes; Francisco M. Benitez
- Web page: https://patentgrep.com/patent/US4391961A

## CPC

- C08F 240/00: Copolymers of hydrocarbons and mineral oils, e.g. petroleum resins
- Y10S 526/943: Polymerization with metallocene catalysts
- C08F: MACROMOLECULAR COMPOUNDS OBTAINED BY REACTIONS ONLY INVOLVING CARBON-TO-CARBON UNSATURATED BONDS
- Y10S: TECHNICAL SUBJECTS COVERED BY FORMER USPC CROSS-REFERENCE ART COLLECTIONS [XRACs] AND DIGESTS

## Abstract

Petroleum resins of lightened color while retaining satisfactory melting point and compatibility are provided by a process which comprises heat soaking a petroleum cracking or reforming fraction containing cationically polymerizable hydrocarbons and from 2 to more than 0.5 weight percent of cyclodienes until the cyclodiene content is no more than 0.5 weight percent distilling said heat soaked petroleum fraction and polymerizing said distilled petroleum fraction in the presence of a polymerization catalyst.

## Claims

### Claim 1

A process for producing a hydrocarbon resin of improved color and thermal stability which comprises heat soaking a petroleum cracking or reforming fraction containing cationically polymerizable hydrocarbons including from more than 0.5 to 2 weight percent of cyclodienes until the cyclodiene content is no more than 0.5 weight percent and the piperylene to cyclopentadiene weight ratio is above at least 50, distilling said heat soaked petroleum fraction, polymerizing said distilled petroleum fraction in the presence of an aluminum halide catalyst and recovering a resin having a Gardner color of no greater than 4 when measured on a solution of equal weights of said resin and toluene.

### Claim 2 (depends on 1)

The process of claim 1 wherein said heat soaking is continued until the cyclodiene content is no more than 0.2 wt% and said weight ratio is greater than 100.

### Claim 3 (depends on 2)

The process of claim 2 wherein said weight ratio is at least 200.

### Claim 4 (depends on 1)

The process of claim 1 wherein said heat soaking of said fraction is at a temperature of from 135.degree. C. to 160.degree. C. for a period of up to 5 hours.