Non-starch containing aqueous sizing composition for glass fibers and sized glass fibers for use in reinforcing elastomers
AssigneePPG Industries, Inc.
InventorMikhail M. Girgis
Life of this patent
Estimating the term…
Abstract
An aqueous treating composition is provided for glass fibers to produce treated glass fiber strands for use in manufacturing cord of glass fibers for reinforcing elastomeric materials, wherein the glass fibers have a more continuous film of the residue of the aqueous treating composition, and improved wettability. The aqueous treating composition is a non-starch-containing treating composition having one or more water dispersible, high molecular weight polyoxyalkylene polyols, one or more silane coupling agents and one or more cationic lubricants.
Claims12
An aqueous non-starch-containing composition for treating glass fibers to produce treated glass fibers to be further treated with an aqueous adhesive coating composition to reinforce elastomeric materials, consisting essentially of:
- A. about 0.5 to about 5 weight percent of one or more water dispersible, high molecular weight polyols selected from the group consisting of polyoxy alkylene polyols and polyalkylene polyols having an average molecular weight from about 300 to about 12,000 and mixtures thereof present as flexible film formers,
- B. about 0.1 to about 2 weight percent of one or more silane coupling agents,
- C. about 0.1 to about 4 weight percent of a cationic lubricant,
- D. water in the amount to give a total solids content for the aqueous composition in the range of about 3 to about 20 weight percent.
An aqueous non-starch-containing composition for treating glass fibers to produce treated glass fibers to be further treated with an aqueous adhesive coating composition to reinforce elastomeric materials, consisting essentially of:
- A. about 0.5 to about 5 weight percent of one or more water dispersible, high molecular weight polyols selected from the group consisting of polyoxyalkylene polyols and polyalkylene polyols having an average molecular weight from about 300 to about 12,000 and mixtures thereof present as flexible film forming materials to provide a more continuous and uniform film and better wettability than that provided by starch on the surface of the glass fibers,
- B. about 0.1 to about 2 weight percent of one or more silane coupling agents,
- C. about 0.1 to about 4 weight percent of a cationic lubricant,
- D. water in the amount to give a total solids content for the aqueous composition in the range of about 3 to about 20 weight percent.
Dependencies are inferred from the claim text.