Method for preparing thermosetting resins
AssigneeAshland Oil, Inc.
InventorsRichard S. Chu, Maher L. Mansour
Life of this patent
Estimating the term…
Abstract
Method and apparatus for preparing a thermosetting resin for further processing. The resin is poured from a batch reactor onto a continuously moving conveyor belt to form a layer of about 2 to 4 inches thick. After the batch is received on the conveyor, the conveyor is stopped for several hours to permit the batch to cool and solidify. Thereafter, the conveyor is restarted and a chopper at the downstream end of the conveyor chops the solidified batch into small chunks and flakes. The conveyor has a rigid trough support under the upstream end of the conveyor's upper run and roller assemblies holding the conveyor in a trough configuration at its downstream end.
Claims4
The method of preparing a thermosetting resin for subsequent molding operations comprising the steps of,
- pouring a partially reacted batch of resin onto a continuously moving belt,
- driving said belt at a lineal speed in relation to the speed of the pour to create a layer of resin on said belt which is approximately 2 to 4 inches thick, the layer being thin enough to permit said resin to cool reasonably rapidly to stop the thermosetting reaction well short of completion,
- stopping said belt after said complete batch of resin has been poured onto it until said batch has cooled to approximately room temperature,
- restarting said belt after said batch has cooled and solidified,
- and chopping said solidified batch into chunks at the downstream end of said conveyor.
The method of preparing a thermosetting phenol formaldehyde resin for subsequent molding operations comprising the steps of,
- pouring a partially reacted batch of resin onto a continuously moving belt,
- driving said belt at a lineal speed in relation to the speed of the pour to create a layer of resin on said belt which is aproximately 2 to 4 inches thick, the layer being thin enough to permit said resin to cool reasonably rapidly to stop the thermosetting reaction well short of completion,
- stopping said belt after said complete batch of resin has been poured onto it until said batch has cooled to aproximately room temperature,
- restarting said belt after said batch has cooled and solidified,
- and chopping said solidified batch into chunks at the downstream end of said conveyor.