US 4,381,948 A · Anhydrous kaolin clay pigment and method of preparation

Abstract

An anhydrous white kaolin clay pigment is disclosed, which consists of porous aggregates of kaolin clay platelets. The pigment exhibits exceptionally high light-scattering ability when incorporated as a filler in paper. The aggregates have an average specific gravity in the range of 0.5 to 0.6, and a size distribution such that not more than 5% by weight thereof are of greater than 10 microns ESD, at least 75% are of less than 2 microns ESD, and not more than 15% are of less than 1 micron ESD. The pigment has a Valley abrasion value below 30 mg, and preferably below 20 mg, and a GE brightness of at least 93. The mean size of the internal pores in the aggregates is less than 0.55 microns and preferably is less than 0.5 microns. This low mean pore size is deemed instrumental in producing the aforementioned high scattering ability. A method for producing the said pigment is also disclosed and claimed.

Claims8

Dependent claims

An anhydrous white kaolin clay pigment having high light scattering when incorporated as a filler in paper, said pigment consisting of porous aggregates formed from sub-micron sized kaolin clay platelets obtained by classification of a dispersed kaolin clay to a 100% less than one micron ESD fraction, said aggregates having an average specific gravity in the range of 0.5 to 0.6 and a mean internal pore size of less than 0.55 microns;

the size distribution of said aggregates being such that not more than 5% by weight thereof are greater than 10 microns ESD, at least 75% are of less than 2 microns ESD, and not more than 15% by weight are of less than 1 micron ESD;
said pigment having a Valley abrasion value below 30 mg, and a GE brightness of at least 93.

A method for producing an anhydrous high-brightness white kaolin clay pigment having enhanced light-scattering properties when incorporated as a filler in paper;

said method comprising:
blunging and dispersing a crude kaolin clay, to form an aqueous dispersion of same;
said crude clay including a total of not more than 0.5% by weight of glass-forming metal oxides, and not more than 1.5% by weight of iron, expressed as Fe.sub.2 O.sub.3, nor more than 2% by weight of titanium, expressed as TiO.sub.2 ;
subjecting said aqueous clay dispersion to a particle size separation, and recovering from said separation a slurry of said clay, wherein 100% by weight of the particles are of less than 1 micron ESD;
drying said slurry to produce a moisture-free clay;
milling said clay to break up agglomerates;
calcining the milled clay product by heating same to a temperature of at least 900.degree. C., and under conditions such that substantially none of said clay is heated to a temperature in excess of 1100.degree. C.;
and
cooling the product of said calcination step and milling same to provide a pigment consisting of porous high light-scattering aggregates of kaolin clay platelets, said aggregates having an average specific gravity in the range of 0.5 to 0.6 and a mean internal pore size of less than 0.55 microns;
the size distribution of said aggregates being such that not more than 5% by weight thereof are greater than 10 microns ESD, at least 75% are of less than 2 microns ESD, and not more than 15% by weight are of less than 1 micron ESD;
said pigment having a Valley abrasion value below 30 mg, and a GE brightness of at least 93.

8 more elements

Dependencies are inferred from the claim text.

Anhydrous kaolin clay pigment and method of preparation

Life of this patent

Anhydrous kaolin clay pigment and method of preparation

Life of this patent

Abstract

Claims8