Method for improving surface defect of specific steel resistant to concentrated nitric acid

A method for reducing surface defects of specific steel resistant to concentrated nitric acid, wherein the specific steel is either stainless steel comprising carbon in an amount of not more than 0.1% (C.ltoreq.0.1%),

• silicon in an amount from not less than 2.5% to not more than 5.0% (2.5.ltoreq.Si.ltoreq.5%),
• manganese in an amount of not more than 2% (Mn.ltoreq.2%),
• chromium in an amount from not less than 15% to not more than 20% (15.ltoreq.Cr.ltoreq.20%),
• nickel in an amount from not less than 10% to not more than 22% (10.ltoreq.Ni.ltoreq.22%),
• at least one of niobium, tantalum and zirconium in an amount from not less than 10 times the carbon content to not more than 2.5% (C.times.10.ltoreq.Nb, Ta and/or Zr.ltoreq.2.5%),
• and the balance being iron and inevitable impurities, or a high-silicon-nickel-chromium steel comprising:
• carbon in an amount of not more than 0.03% (C.ltoreq.0.03%),
• silicon in an amount from more than 5% to not more than 7% (5.ltoreq.Si.ltoreq.7%),
• manganese in an amount of not more than 10% (Mn.ltoreq.10%),
• chromium in an amount from not less than 7% to not more than 16%,
• nickel in an amount from not less than 10% to less than 19% (10.ltoreq.Ni.ltoreq.19%),
• at least one of niobium, tantalum and zirconium in an amount from not less than 4 times the carbon content to not more than 2%,
• and the balance being iron and inevitable impurities, characterized by adding titanium in an amount from not less than 0.05% to not more than 0.2% (0.05.ltoreq.Ti.ltoreq.0.2%) to melted steel and thereafter removing titanium slag when producing said steel, percentages being by weight.