Process for producing hollow fibres having a uniform wall thickness and a non-uniform cross-sectional area
AssigneeExtracorporeal Medical Specialties, Inc.
InventorJohn A. Taylor
Life of this patent
Estimating the term…
Abstract
Hollow fibers, particularly useful as semipermeable membranes in separatory devices such as blood dialyzers, having a non-uniform cross-sectional area along the length thereof. The fibers have recurring points of maximum outside diameter and minimum outside diameter and such points may recur on a regular basis or at random. Fiber wall thicknesses may be substantially uniform or non-uniform. Methods and apparatus for making the fibers are disclosed.
Claims14
A method for producing a hollow fiber having a hollow core extending continuously throughout the length thereof, said fiber having a uniform wall thickness and a non-uniform cross-sectional area, said method comprising
- (a) providing a tube-in-orifice spinneret comprising a housing having a chamber communicating with an outer surface thereof and a hollow tube having a continuous lumen extending the length thereof secured within said chamber, the walls of said chamber and the outer surface of said tube defining an annular space through which a fiber forming material may be extruded;
- (b) supplying a fiber forming material to said chamber at a constant mean flow rate while simultaneously varying the pressure on said supplied fiber forming material;
- (c) extruding said fiber forming material through said annular space to form a hollow core extrudate;
- (d) supplying a fluid at a constant mean flow rate to the lumen of said hollow tube while simultaneously varying the pressure on said supplied fluid, the pressure variations on said supplied fluid being synchronized with the pressure variations on said supplied fiber forming material;
- (e) removing from the exit of said spinneret said extrudate with said fluid contained in the hollow core thereof;
- (f) converting said fiber forming material to fiber form.
A method for producing a cuproammonium regenerated cellulose hollow fiber having a hollow core extending continuously throughout the length thereof, said fiber having a substantially uniform wall thickness and a non-uniform cross-sectional area, said method comprising
- (a) providing a tube-in-orifice spinneret comprising a housing having a chamber communicating with an outer surface thereof and a hollow tube having a continuous lumen extending the length thereof secured within said chamber, the walls of said chamber and the outer surface of said tube defining an annular space through which a fiber forming material may be extruded;
- (b) supplying a cuproammonium cellulose solution to said chamber at a constant mean flow rate while simultaneously varying the pressure on said supplied solution;
- (c) extruding said cuproammonium cellulose solution through said annular space to form a hollow core extrudate;
- (d) supplying isopropyl myristate at a constant mean flow rate to the lumen of said hollow tube while simultaneously varying the pressure on said supplied fluid, the pressure variations on said supplied isopropyl myristate being synchronized with the pressure variations on said supplied solution;
- (e) removing from the exit of said spinneret said extrudate with said fluid contained in the hollow core thereof;
- and
- (f) converting said cuproammonium cellulose solution to fiber form.
A method for producing a cuproammonium regenerated cellulose hollow fiber having a hollow core extending a continuously throughout the length thereof, said fiber having a substantially uniform wall thickness and a non-uniform cross-sectional area, said method comprising:
- (a) providing a tube-in-orifice spinneret comprising housing having a chamber communicating with an outer surface thereof and a holow tube having a continuous lumen extending the length thereof secured within said chamber, the walls of said chamber and the outer surface of said tube defining an annular space through which a fiber-forming material may be extruded;
- (b) supplying a cuprammonium cellulose solution to said chamber at a constant mean flow rate while simultaneously varying the pressure on said suppied solution;
- (c) extruding said cuprammonium cellulose solution through said annular space to form a hollow core extrudate;
- (d) supplying a fluid at a constant mean flow rate to the lumen of said hollow tube while simultaneously varying the pressure on said supplied fluid, the pressure variations on said suppied fluid being synchronized with the pressure variations on said supplied cuprammonium cellulose solution;
- (e) removing from the exit of said spinneret said extrudate with said fluid contained in the hollow core thereof;
- and
- (f) converting said cuprammonium cellulose solution to fiber form