# US 4,379,889 A · Process for producing polybutadine rubber with enhanced mechanical strength > Agents: this data is available as JSON from the patentgrep API and MCP server — see https://patentgrep.com/llms.txt - Number: US 4,379,889 A - Document ID: US4379889A - Status: Granted - Kind: A - Application number: 06/216,869 - Filed: 1980-12-16 - Granted: 1983-04-12 - Earliest claimed: 1979-12-20 - Assignees: Ube Industries, Ltd. - Inventors: Hidetomo Ashitaka; Kyohei Oizumi; Kazuya Jinda; Kazutoshi Inaishi - Web page: https://patentgrep.com/patent/US4379889A ## CPC - C08F 295/00: Macromolecular compounds obtained by polymerisation using successively different catalyst types without deactivating the intermediate polymer - C08F 136/06: Butadiene - C08F: MACROMOLECULAR COMPOUNDS OBTAINED BY REACTIONS ONLY INVOLVING CARBON-TO-CARBON UNSATURATED BONDS ## Abstract A polybutadiene rubber having an enhanced mechanical strength is produced by a process comprising two successive steps of: (A) cis-1,4-polymerizing 1,3-butadiene in a polymerization medium in the presence of a catalyst comprising a cobalt compound and a dialkyl aluminium halide of the formula (I): AlR.sub.2 X, wherein R=C.sub.2 -8 alkyl and X=halogen, and; (B) subjecting a mixture of the resultant cis-1,4-polybutadiene and the non-reacted 1,3-butadiene in the polymerization medium to a 1,2-polymerization in the presence of a catalyst comprising a cobalt compound, a dialkyl aluminium halide of the formula (I), carbon disulfide and an electron donative organic compound. ## Claims ### Claim 1 A process for producing a polybutadiene rubber with enhanced mechanical strength, comprising the two successive steps of: (A) polymerizing a first polymerization mixture comprising 1,3-butadiene and a polymerization medium in the presence of a cis-1,4-polymerization catalyst which comprises: (1) a cobalt compound selected from the group consisting of cobalt complexes with beta-diketones of the formula (II): ##STR3## wherein R.sup.1 and R.sup.2 represent an aliphatic hydrocarbon radical having 1 to 3 carbon atoms, respectively, and R.sup.3 and R.sup.4 represent at least one member selected from the group consisting of a hydrogen atom and an aliphatic hydrocarbon radical having 1 to 3 carbon atoms, respectively; a cobalt complex with .beta.-keto acid esters of formula (III): ##STR4## wherein R.sup.1, R.sup.2, R.sup.3 and R.sup.4 are as defined above; cobalt salts of an organic carboxylic acid having 6 or more carbon atoms; and a cobalt halide complex of the formula (IV): CoXnYm (IV) wherein X represents a halogen atom, n represents an integer of 2 or 3, Y represents an organic ligand capable of forming a complex in coordination with the cobalt halide and m represents an integer of from 1 to 4, and (2) a dialkyl aluminum halide of the formula (I): AlR.sub.2 X (I) wherein R represents an alkyl radical having 2 to 8 carbon atoms and X represents a halogen atom, to convert at least a portion of the amount of said 1,3-butadiene to a cis-1,4-polybutadiene; and (B) polymerizing a second polymerization mixture comprising the resultant cis-1,4-polybutadiene from Step (A), unreacted 1,3-butadiene and a polymerization medium in the presence of a 1,2-polymerization catalyst which comprises: 1. said cobalt compound; 2. said dialkyl aluminum halide; 3. carbon disulfide; and 4. an electron donor organic compound selected from the group consisting of an aliphatic polyether, an aliphatic carboxylic ester, an aliphatic ketone, an aliphatic acetal, an aliphatic N,N-dialkyl amide, an aliphatic dialkyl sulfoxide and a trialkyl phosphate, to convert said cis-1,4-polybutadiene and said 1,3-butadiene to a polybutadiene rubber, whereby the resultant polybutadiene rubber comprises 70% to 95% by weight of a boiling n-hexane-soluble fraction thereof having an intrinsic viscosity of from 1 to 5 determined in toluene at a temperature of 30.degree. C. and containing 95% or more of a cis-1,4-structure, and 5% to 30% by weight of a boiling n-hexane-insoluble fraction having a reduced viscosity of from 0.5 to 5, determined in tetrahydronaphthalene at a temperature of 135.degree. C., and a melting point of 180.degree. C. or more, and containing 85% or more of a 1,2-structure. ### Claim 2 (depends on 1) A process as claimed in claim 1, wherein said dialkyl aluminium halide of the formula (I) is diethyl aluminium chloride. ### Claim 3 (depends on 1) A process as claimed in claim 1, wherein said cis-1,4-polymerization catalyst used contains 0.005 millimoles or more of said cobalt compound and 0.5 millimoles or more of said dialkyl aluminium halide per mole of said 1,3-butadiene contained in said first polymerization mixture. ### Claim 4 (depends on 1) A process as claimed in claim 1, wherein the molar ratio of the amount of said dialkyl aluminium halide to the amount of said cobalt compound in said cis-1,4-polymerization catalyst is 5:1 or more. ### Claim 5 (depends on 1) A process as claimed in claim 1, wherein said first polymerization medium is an organic solvent capable of dissolving said cis-1,4-polybutadiene. ### Claim 6 (depends on 5) A process as claimed in claim 5, wherein said first polymerization medium contains 5 to 50 mg/l of water. ### Claim 7 (depends on 1) A process as claimed in claim 1, wherein said first polymerization is carried out at a temperature of from -20.degree. to 80.degree. C. ### Claim 8 (depends on 1) A process as claimed in claim 1, wherein the content of 1,3-butadiene in said first polymerization mixture is in the range of from 5 to 40% based on the entire weight of the first polymerization mixture. ### Claim 9 (depends on 1) A process as claimed in claim 1, wherein the resultant cis-1,4-polybutadiene contains 90% or more of cis-1,4-structure, and has an intrinsic viscosity of from 1 to 4, determined in toluene at a temperature of 30.degree. C. ### Claim 10 (depends on 1) A process as claimed in claim 1, wherein said carbon disulfide contains substantially no water. ### Claim 11 (depends on 1) A process as claimed in claim 1, wherein said 1,2-polymerization catalyst used contains from 0.005 to 0.5 millimoles of said cobalt compound, from 0.1 to 50 millimoles of said dialkyl aluminium halide, from 0.01 to 10 millimoles of said carbon disulfide and from 0.05 to 5 millimoles of said electron donative organic compound, per mole of the non-reacted 1,3-butadiene used. ### Claim 12 (depends on 1) A process as claimed in claim 1, wherein said 1,2-polymerization catalyst, the molar ratio of the amount of said dialkyl aluminium halide to the amount of said cobalt compound is 5:1 or more. ### Claim 13 (depends on 1) A process as claimed in claim 1, wherein the sum of the molar amounts of said electron donative organic compound and water contained in said second polymerization mixture is less than the molar amount of said dialkyl aluminium halide. ### Claim 14 (depends on 1) A process as claimed in claim 1, wherein said second polymerization is carried out at a temperature of from -20.degree. to 80.degree. C. ### Claim 15 (depends on 1) A process as claimed in claim 1, wherein the content of the non-reacted 1,3-butadiene in said second polymerization mixture is in the range of from 3 to 40% by weight. ### Claim 16 (depends on 1) A process as claimed in claim 1, wherein the amount of 1,3-butadiene cis-1,4-polymerized in said first polymerization is in the range of 70 to 95% based on the entire weight of the polymerized 1,3-butadiene in this process. ### Claim 17 (depends on 1) A process as claimed in claim 1, wherein the amount of 1,3-butadiene 1,2-polymerized in said second polymerization is in the range of 5 to 30% based on the entire weight of the polymerized 1,3-butadiene in this process.