Binder for casting sand and resin-coated grains of sand
AssigneesDaicel Chemical Industries, Ltd., Shinto Kogio, Ltd.
InventorsKazuyuki Nishikawa, Katsumi Hirao
Life of this patent
Estimating the term…
Abstract
A binder for casting sand of the present invention comprises 5-95 wt. % of cellulose acetate and 5-95 wt. % of a thermosetting resin precondensate such as an alkylated methylolmelamine, alkylated methylolurea or a mixture of them, and it is used particularly for the casting carried out at a relatively low casting temperature. Up to about 50% of cellulose acetate may be replaced with an acetate of an aliphatic polyhydric alcohol or an alkyl phthalate. In the resin-coated grains of sand of the present invention, the grains of sand are coated with a binder comprising 5-95 wt. % of cellulose acetate and 5-95 wt. % of a thermosetting resin precondensate.
Claims7
A composition consisting essentially of a mixture of approximately 43 to 60 wt. % of cellulose acetate which is soluble in acetone, has an acetylation degree of from 48 to 57% and has a limiting viscosity number of from 0.15 to 2.2 measured in an acetone solution thereof at 25.degree. C., from 17 to 20 wt. % of a plasticizer for said cellulose acetate, and from 20 to 40 wt. % of a thermosetting resin precondensate selected from the group consisting of acetone-soluble alkylated methylolmelamines, acetone-soluble alkylated methylolureas and mixtures thereof.
A composition consisting essentially of a mixture of from 20 to 33 wt. % of cellulose acetate which is soluble in acetone, has an acetylation degree of from 48 to 57% and has a limiting viscosity number of from 0.15 to 2.2 measured in an acetone solution thereof at 25.degree. C., and from 67 to 80 wt. % of a thermosetting resin precondensate selected from the group consisting of acetone-soluble alkylated methylolmelamines, acetone-soluble alkylated methylolureas and mixtures thereof.
Grains of sand coated with an effective binder amount of a binder composition consisting essentially of a mixture of
- A. from 5 to 95 wt. % of a component selected from the group consisting of (1) cellulose acetate which is soluble in acetone, has an acetylation degree of from 48 to 57% and has a limiting viscosity number of from 0.15 to 2.2 measured in an acetone solution thereof at 25.degree. C., and (2) a mixture of said cellulose acetate and up to 50%, based on the weight of component A, of a plasticizer for said cellulose acetate, and
- B. from 95 to 5 wt. % of a thermosetting resin precondensate selected from the group consisting of acetone-soluble alkylated methylolmelamines, acetone-soluble alkylated methylolureas and mixtures thereof.
Dependencies are inferred from the claim text.