Screen-printable dielectric composition

A screen-printable dielectric composition for making hermetic dielectrics having an insulation resistance (IR) drop of less than 4 orders of magnitude after submersion in water at 50.degree. C. for 10 days consisting essentially of (a) a perovskite of the formula ATiO.sub.3 in which is A is selected from the group consisting of barium, calcium, strontium and lead, (b) a bismuth-substituted pyrochlore of the formula Bi.sub.2-x M.sub.x M'.sub.2-y M".sub.y O.sub.7-z wherein

• M is a rare earth metal of atomic number 57 to 71, lead, cadmium, or yttrium
• M' is iron, gallium or indium
• M" is antimony, tantalum or niobium,
• X is a number in the range 0-1,
• y is a number in the range 1-1.5 and
• Z is a number in the range 0-0.5 and
• (c) a low temperature-melting devitrifiable glass having a specific viscosity (log .eta.) of less than 6 at the firing temperature dispersed in an inert liquid vehicle in which the glass has a softening point below 600.degree. C. and in which the relative proportions of the components, by weight, are 10-65% (a) 10-70% (b) and 1-20% (c).

An hermetic capacitor having an insulation resistance (IR) drop of less than 4 order of magnitude after submersion in water at 50.degree. C. for 10 days and comprising (1) a first conductor terminal on which is printed (2) an hermetic dielectric film and (3) a second conductor terminal overlying the dielectric film, the dielectric layer consisting of (a) a perovskite of the formula ATiO.sub.3 in which is A is selected from the group consisting of barium, calcium, strontium and lead, (b) a bismuth-substituted pyrochlore of the formula Bi.sub.2-x M.sub.x M'.sub.2-y M".sub.y O.sub.7-z wherein

• M is a rare earth metal of atomic number 57 to 71, lead, cadmium, or yttrium
• M' is iron, gallium or indium
• M" is antimony, tantalum or niobium,
• X is a number in the range 0-1,
• y is a number in the range 1-1.5 and
• Z is a number in the range 0-0.5 and
• (c) a low temperature-melting devitrifiable glass, having a specific viscosity (log .eta.) of less than 6 at the firing temperature the assemblage having been cofired to remove the inert liquid therefrom and to effect liquid phase sintering and then cooled to effect devitrification of the glass in which the glass has a softening point below 600.degree. C. and in which the relative proportions of the components, by weight, are 10-65% (a) 10-70% (b) and 1-20% (c).

An hermetic multilayer capacitor having an insulation resistance (IR) drop of less than 4 order of magnitude after submersion in water at 50.degree. C. for 10 days and comprising a first conductor terminal and a plurality of alternating printed dielectric layers and overlying conductor terminals, the dielectric layers consisting of (a) perovskite of the formula ATiO.sub.3 in which is A is selected from the group consisting of barium, calcium, strontium and lead, (b) a bismuth-substituted pyrochlore of the formula Bi.sub.2-x M.sub.x M'.sub.2-y M".sub.y O.sub.7-z wherein

• M is a rare earth metal of atomic number 57 to 71, lead, cadmium, or yttrium
• M' is iron, gallium or indium
• M" is antimony, tantalum or niobium,
• X is a number in the range 0-1,
• y is a number in the range 1-1.5 and
• Z is a number in the range 0-0.5 and
• (c) a low temperature-melting devitrifiable glass, having a specific viscosity (log .eta.) of less than 6 at the firing temperature the assemblage having been cofired to remove the inert liquid therefrom and to effect liquid phase sintering and then cooled to effect devitrification of the glass in which the glass has a softening point below 600.degree. C. and in which the relative proportions of the components, by weight, are 10-65% (a) 10-70% (b) and 1-20% (c).