Process of making calcium acetate deicing agents
OwnerAlan B. Gancyinventor
Life of this patent
Estimating the term…
Abstract
A process of making a calcium acetate-containing solution having a pH value at room temperature between about 7 and about 8 is provided comprising reacting acetic acid with a carbonate compound, adding calcined limestone, and optionally finishing off the acid-base reaction with an amount of an alkali metal hydroxide comprising from about 2% to about 5% of the total stoichiometric complement to the amount of acetic acid. Further process options which may be used in the preparation of deicing agents include adding coarse limestone to the above-prepared calcium acetate-containing solution in amounts up to 10% by weight and converting the solution into solid flakes.
Claims5
In a process of making a calcium acetate-containing solution having a pH value at room temperature in the range from about 7 to about 8, the steps comprising:
- a. reacting acetic acid and an amount of calcined limestone comprising about 95% to about 98% of the total stoichiometric complement of said acetic acid;
- and
- b. adding an alkali metal hydroxide in an amount comprising from about 2% to about 5% of said total stoichiometric complement.
In a process of making a calcium acetate-containing solution having a pH value at room temperature in the range from about 7 to about 8, the steps comprising:
- a. completely reacting a carbonate with acetic acid, wherein the amount of said carbonate comprises from about 50% to about 70% of the total stoichiometric complement of said acid;
- b. adding calcined limestone in an amount comprising from about 25% to about 50% of said total stoichiometric complement;
- and
- c. adding an alkali metal hydroxide in an amount comprising from about 2% to about 5% of said total stoichiometric complement.
In a process of making a calcium-acetate containing deicing agent, the steps comprising:
- a. adding coarse limestone to a calcium acetate-containing solution;
- b. agitating the calcium acetate-coarse limestone suspension;
- and
- c. converting said suspension into a substantially solid deicing agent.
In a process of making calcium acetate-containing solid flakes, the steps comprising:
- a. removing water from a substantially saturated calcium acetate-containing solution by heating the solution to form a solid calcium acetate-containing product.
Dependencies are inferred from the claim text.