Method of making a coated cutting tip
AssigneeNgk Spark Plug Co., Ltd.
InventorsJunichiro Suzuki, Hiroshi Tanaka
Life of this patent
Estimating the term…
Abstract
A method of making a coated tip for cutting purposes having a lower degree of flank and crater wear and reduced chipping. A WC-based ultrahard alloy containing WC, at least one nitride selected from among TiN, TaN and NbN and a bonding metal is heat treated at a temperature of 800.degree. C. to 1,300.degree. C. in a nitrogen atmosphere for a sufficiently long period of time to cause nitride in a layer in the vicinity of the surface of the alloy to move to the surface to form a layer of nitride thereon as well as an alloy layer of WC and the bonding metal in which the nitride has been reduced. The surface of the tip is then coated with a layer of Al.sub.2 O.sub.3.
Claims4
A method of making a coated tip for cutting purposes, comprising the steps of heat treating a WC-based ultrahard alloy containing WC, at least one nitride selected from the group consisting of TiN, TaN and NbN, and a bonding metal at a temperature of 800.degree. C. to 1,300.degree. C. ;
- in an atmosphere containing nitrogen for a sufficient time to cause said nitride in a layer in the vicinity of the surface of said alloy to move to said surface to form a layer of said nitride on said surface and to form an alloy layer of said WC and said bonding metal in which said nitride has been reduced;
- and coating said surface with a layer of Al.sub.2 O.sub.3.
A method of making a coated tip for cutting purposes, comprising the steps of heat treating a WC-based ultrahard alloy containing WC, at least one nitride selected from the group consisting of TiN, TaN and NbN, and a bonding metal at a temperature of approximately 1,200.degree. C. for approximately 2 hours in a nitrogen atmosphere to form a nitride layer having a thickness of 1 to 7.mu. on the surface of said tip;
- placing said tip in a reaction chamber;
- and heating set tip in said reaction chamber to a temperature of approximately 1,100.degree. C. while supplying a gas mixture containing approximately 59% of H.sub.2, 3% of Co and Co.sub.2, and 8% of AlCl.sub.3 at a pressure of approximately 20 Torr of approximately 2 hours.
Dependencies are inferred from the claim text.