Preparation of improved heat stable yellow iron oxide pigments
AssigneeTitan Kogyo K.K. Japan
InventorsJihei Senda, Yoshihiro Inoue, Toshiaki Uenishi, Hidefumi Harada, Kouji Nakata, Akio Akagi
Life of this patent
Estimating the term…
Abstract
Yellow iron oxide pigments having improved heat stability are prepared by subjecting an alkaline slurry of conventional yellow iron oxide, a soluble ferric salt, and sodium aluminate to a hydrothermal (autoclave) treatment at 100.degree.-240.degree. C., separating and slurrying the resultant solid product, and subjecting that product to a second hydrothermal treatment of 250.degree.-350.degree. C. The original iron oxide has a heat stability (based on color change from yellow to red) temperature of about 203.degree. C., while the final product shows a change at 270.degree. C.
Claims6
The preparation of a yellow iron oxide pigment having improved heat stability, comprising the steps of
- (a) forming an aqueous slurry of from about 30 to about 200 parts yellow iron oxide (.alpha.-FeOOH), from about 1 to about 100 parts a soluble ferric salt, selected from the group consisting of ferric sulfate, ferric chloride, ferric nitrate, ferric oxalate, and ferric thiocyanate, an alkali metal hydroxide in an amount to provide the slurry with a pH of greater than 10 , and from about 20 to about 100 parts of a water-soluble or alkali-soluble aluminum compound, selected from the group consisting of sodium aluminate, potassium aluminate, aluminum chloride, potash alum, and aluminum nitrate, all based on 1000 parts water,
- (b) subjecting the resultant mixture to a first hydrothermal treatment carried out at a temperature of from about 100.degree. C. to about 240.degree. C. for a time greater than 30 minutes,
- (c) separating the treated mixture into a first solid phase and a first liquid phase,
- (d) dispersing the first solid phase of step (c) in water,
- (e) subjecting the first solid phase to a second hydrothermal treatment at a temperature of at least 250.degree. C. to about 350.degree. C. for a time greater than 30 minutes,
- (f) separating the treated mixture into a second solid phase and a second liquid phase, and
- (g) recovering the second solid phase and processing said phase to give a treated yellow iron pigment having an improved heat stability.
The preparation of a yellow iron oxide pigment having improved heat stability, comprising the steps of
- (a) forming an aqueous slurry of a treated yellow iron oxide pigment that has been previously subjected to the treatment steps of
- 1. forming an aqueous slurry of yellow iron oxide (.alpha.-FeOOH), and sodium hydroxide,
- 2. subjecting the resultant slurry to a hydrothermal treatment at a temperature of from about 100.degree. C. to about 240.degree. C. for a period of between about 1/2 hour and about 5 hours, and
- 3. separating the treated mixture into a solid phase and a liquid phase, with the solid phase being further processed to form the slurry of the pretreated yellow iron oxide,
- (b) adding to a slurry of from about 30 to about 200 parts of the pretreated yellow iron oxide based on 1000 parts water, from about 1 to about 100 parts of a soluble ferric salt, selected from the group consisting of ferric sulfate, ferric chloride, ferric nitrate, ferric oxalate, and ferric thiocyanate, an amount of alkali metal hydroxide to provide the slurry with a pH of greater than 10 and from about 20 to 100 parts of a water-soluble or alkali-soluble aluminum compound, selected from the group consisting of sodium aluminate, potassium aluminate, aluminum chloride, potassium alum, and aluminum nitrate, all based on 1000 parts water,
- (c) subjecting the slurry mixture to a first hydrothermal treatment at a temperature of from about 100.degree. C. to about 240.degree. C. for a time greater than 30 minutes,
- (d) separating the treated mixture into a solid phase and a liquid phase,
- (e) dispersing the solid phase in water,
- (f) subjecting the resultant slurry to a second hydrothermal treatment, and at a temperature of at least 250.degree. C. to about 350.degree. C. for longer than 30 minutes, and
- (g) recovering the solid phase from the treatment and processing said phase to give a product having a heat stability temperature higher than the heat stability temperature of the treated iron oxide of step (a).
Dependencies are inferred from the claim text.