Loading patent…
AssigneeRohm Co., Ltd.
InventorsKlaus Kerk, Dieter Mueller, Bernd Oleiko
Estimating the term…
What is disclosed is a rigid, one-piece, shaped body, made of a biaxially stretched synthetic resin in the form of a sheet at least 1 mm thick, the edge of which does not lie in a single plane, and the surface of which is smaller than a flat initial surface enclosed by the edge and preferably approximates the mathematically minimum surface enclosed by the edge, is suitable according to the invention as a lightweight building element having high resistance to buckling. The new shaped bodies are made by shaping a flat sheet of biaxially stretched synthetic resin at least 1 mm thick, while in the thermoelastic state, so that the edge of the sheet is brought into a configuration which does not lie in one plane, and the surface enclosed by the edge is allowed to shrink back partially while in the thermoelastic state, whereby a shrinkage of the edge of the sheet is prevented by clamping the edge, and the resulting shaped body is cooled below the softening temperature before the edge clamping is loosened.
A method for making a rigid one-piece shaped body of biaxially stretched synthetic resin in the form of a sheet having a thickness of at least 1 millimeter, said body having an edge which does not lie in one plane and having a surface smaller than the imagined flat initial surface enclosed by said edge, which method comprises deforming a sheet of biaxially stretched synthetic resin at least 1 millimeter thick by elastic bending at a temperature below the softening point of the resin into a configuration in which the edge of the sheet does not lie in a single plane, rigidly fixing the edge of the sheet, and heating said sheet without touching the surface thereof and with equal gas pressure on both sides of the sheet until said synthetic resin is in the thermoelastic state, whereby the surface of the sheet enclosed by the edge shrinks back partially but shrinkage of the edge of the sheet is not permitted, and subsequently cooling the sheet below the softening temperature of the synthetic resin.
A method for making a rigid one-piece shaped body of biaxially stretched synthetic resin in the form of a sheet having a thickness of at least 1 millimeter, said body having an edge which does not lie in one plane and having a surface smaller than the imagined flat initial surface enclosed by said edge, which method comprises rigidly fixing the edge of a sheet of biaxially stretched synthetic resin at least 1 millimeter thick, heating said sheet without touching the surface thereof and with equal gas pressure on both sides of the sheet until said synthetic resin is in the thermoelastic state, and deforming said heated sheet into a configuration in which the edge of the sheet does not lie in a single plane, whereby the surface of the sheet enclosed by the edge shrinks back partially but shrinkage of the edge of the sheet is not permitted, and subsequently cooling the sheet below the softening point of the synthetic resin.
A method for making a rigid one-piece shaped body of biaxially stretched synthetic resin in the form of a sheet having a thickness of at least 1 millimeter, said body having an edge which does not lie in one plane and having a surface smaller than the imagined flat initial surface enclosed by said edge, which method comprises first folding a sheet of said biaxially stretched resin along at least one fold line by heating said resin above its softening point in a small zone along said fold line and deforming the sheet so that the edge of said sheet is no longer in a single plane, then rigidly fixing the edge of the deformed sheet and heating said sheet without touching the surface thereof and with equal gas pressure on both sides of said sheet until said synthetic resin is in the thermoelastic state, whereby the surface of the sheet enclosed by the edge shrinks back partially but shrinkage of the edge of the sheet is not permitted, and subsequently cooling the sheet below the softening temperature of the synthetic resin.
Dependencies are inferred from the claim text.