Method of increasing the strength of carbon and graphite members
AssigneeSigri Elektrographit GmbH
InventorsGuido Gistinger, Manfred Schmid
Life of this patent
Estimating the term…
Abstract
Increasing the strength and improving other properties of porous carbon or graphite bodies by immersing the porous body in a mixture containing 35-70% hardenable resin and 30 to 65% volatile solvent to impregnate pores. The impregnated porous body is heated to 120.degree. to 180.degree. C. to harden the resin. Carbonization of the body is effected by heating in an inert atmosphere at a rate of at least 3 K/hr to 800.degree.-1300.degree. C. Improved strength bodies are obtained with a single impregnation and single carbonizing step.
Claims8
Method of increasing the strength of a porous carbon or graphite body formed from a mixture of granular carbon-containing substances with a carbonizable binder and heating in the absence of air to carbonize the binder which comprises subjecting said body to a single resin impregnation and carbonization by
- (a) immersing the porous body in a mixture in which 35 to 70% by weight of a hardenable resin containing an aldehyde, selected from the group consisting of phenol-formaldehyde resins, furan resins and melamine resins is admixed with 30 to 65% by weight of a volatile liquid, organic solvent and in the absence of colloidal graphite, to impregnate the pores of the porous body with said mixture;
- (b) Heating the impregnated porous body to a temperature of 120.degree. to 180.degree. C. to effect hardening the resin in said pores;
- and
- (c) carbonizing the impregnating medium by heating in an inert or reducing atmosphere at a rate of at least 3 K/hr to a temperature of 800.degree. to 1300.degree. C.