Method for preparing a protective amorphous silicon passivating film on a semiconductor device
AssigneeSiemens Aktiengesellschaft
InventorsFriedrich Dannhauser, Karl Kempter, Jurgen Krausse, Manfred Schnoller
Life of this patent
Estimating the term…
Abstract
In the present invention a process is provided for depositing a protective passivating film of doped or undoped amorphous silicon on a body of semiconductor material. In the process a body of semiconductor material is disposed within a reaction vessel, a silicon-hydrogen gaseous compound is fed into the reaction vessel and decomposed by means of a glow discharge. The decomposition of the silicon-hydrogen gas mixture results in the deposition of amorphous silicon on the semiconductor body.
Claims8
Process for depositing a passivating film of amorphous silicon on a body of silicon semiconductor material, comprising disposing a a semiconductor body in a glow discharge path within a reaction chamber maintained under vacuum, conducting a flow of gaseous silicon-hydrogen compound into said reaction chamber to effect decomposition of the compound by the glow discharge energized by voltage from an external source of electrical power and deposition of a passivating film of amorphous silicon on the semiconductor body maintained in the range of 150.degree. to 350.degree. C., and regulating the operating conditions in the reaction chamber, namely, gaseous silicon-hydrogen pressure, flow rate of gaseous silicon-hydrogen, power in the glow discharge and temperature of the semiconductor body to obtain a content of hydrogen in the amorphous silicon between 5 and 40 atom-percent and a resistivity between 10.sup.8 and 10.sup.10 ohm/cm.
Process for depositing a passivating film of amorphous silicon on a body of silicon semiconductor material, comprising disposing a semiconductor body in a glow discharge path within a reaction chamber maintained under vacuum, conducting a flow of gaseous hydrogen silane (SiH.sub.4) into said reaction chamber to effect decomposition of the hydrogen silane by the glow discharge energized by voltage from an external source of electrical power and deposition of a passivating film of amorphous silicon on the semiconductor body maintained in the range of 150.degree. to 350.degree. C., and regulating the operating conditions in the reaction chamber, namely, gaseous hydrogen silane pressure, flow rate of gaseous hydrogen silane, power in the glow discharge and temperature of the semiconductor body to obtain a content of hydrogen in the amorphous silicon between 5 and 40 atom-percent in which 1.times.10.sup.-4 to 1.times.10.sup.-2, volume percent, of diborane (B.sub.2 H.sub.6) is mixed with the hydrogen silane to obtain a resistivity between 10.sup.9 and 5.times.10.sup.11 ohm/cm.
Process for depositing a passivating film of amorphous silicon on a body of silicon semiconductor material, comprising disposing a semiconductor body in a glow discharge path within a reaction chamber maintained under vacuum, conducting a flow of gaseous hydrogen silane (SiH.sub.4) into said reaction chamber to effect decomposition of the hydrogen silane by the glow discharge energized by voltage from an external source of electrical power and deposition of a passivating film of amorphous silicon on the semiconductor body maintained in the range of 150.degree. to 350.degree. C., and regulating the operating conditions in the reaction chamber, namely, gaseous hydrogen silane pressure, flow rate of gaseous hydrogen silane, power in the glow discharge and temperature of the semiconductor body to obtain a content of hydrogen in the amorphous silicon between 5 and 40 atom-percent in which 10% to 60%, by volume, of ethylene (C.sub.2 H.sub.4) is mixed with the hydrogen silane to obtain a resistivity between 10.sup.10 and 10.sup.11 ohm/cm.
Dependencies are inferred from the claim text.