Method of producing microporous joints in metal bodies
AssigneeThe United States of America as represented by the United States Department of Energy
InventorJoseph C. Danko
Life of this patent
Estimating the term…
Abstract
Tungsten is placed in contact with either molybdenum, tantalum, niobium, vanadium, rhenium, or other metal of atoms having a different diffusion coefficient than tungsten. The metals are heated so that the atoms having the higher diffusion coefficient migrate to the metal having the lower diffusion rate, leaving voids in the higher diffusion coefficient metal. Heating is continued until the voids are interconnected.
Claims3
A process for making a microporous vent at the interface of a joint between two metals having different diffusion coefficients comprising the steps of :
- forming an intimate contact interface joint between two metals, one of the two metals having a higher diffusion coefficient than the other of the two metals and selected from the group consisting of molybdenum, tantalum, niobium, vanadium, rhenium, molybdenum-50 weight % rhenium, and niobium-vanadium, the other metal of the two metals having a lower diffusion coefficient being selected from the group consisting of tungsten and tungsten-25 weight % rhenium,
- heating the thus joined metals to a temperature below their melting point but high enough to cause atoms of the one of the two metals having the higher diffusion coefficient to migrate into the other of the two metals having the lower diffusion coefficient, and
- maintaining the joint metals in the heated condition for a period of time sufficient for voids resulting from the migration of atoms to become interconnected, thereby producing microporous vents at the interface of the joint between the two metals.
Dependencies are inferred from the claim text.