Quick setting water-compatible furfuryl alcohol polymer concretes
AssigneeThe United States of America as represented by the United States Department of Energy
InventorsToshifumi Sugama, Lawrence E. Kukacka, William H. Horn
Life of this patent
Estimating the term…
Abstract
A novel quick setting polymer concrete composite comprising a furfuryl alcohol monomer, an aggregate containing a maximum of 8% by weight water, and about 1-10% trichlorotoluene initiator and about 20-80% powdered metal salt promoter, such as zinc chloride, based on the weight of said monomer, to initiate and promote polymerization of said monomer in the presence of said aggregate, within 1 hour after mixing at a temperature of -20.degree. C. to 40.degree. C., to produce a polymer concrete having a 1 hour compressive strength greater than 2000 psi.
Claims11
A quick setting, water-compatible polymer concrete composition comprising about 8-20% by weight of a furfuryl alcohol monomer, 78-92% of an aggregate system having a maximum pH of about 8 containing filler and 0-8% by weight water, about 1-10% trichlorotoluene based on the weight of said monomer, and about 20-80% metal salt, selected from the class consisting of SnCl.sub.4, ZnCl.sub.2 and AlCl.sub.3, based on the weight of said monomer, to initiate and promote polymerization within one hour at a temperature within the range of -20.degree. C. to 40.degree. C., in the production of a polymer concrete having a one hour compressive strength greater than 2000 psi.
A quick setting, water-compatible polymer concrete composition comprising about 8-20% by weight of a furfuryl alcohol monomer, 78-92% of an aggregate system having a maximum pH of about 8 containing filler and 0-8% by weight water, and 1.5% trichlorotoluene and 60% zinc chloride based on the weight of said monomer to initiate and promote polymerization within one hour at a temperature within the range of -20.degree. C. to 40.degree. C., in the production of a polymer concrete having a one hour compressive strength greater than 2000 psi.
A method of preparing a quick setting, water-compatible polymer concrete composition containing about 8-20% by weight of a furfuryl alcohol monomer 78-92% of an aggregate system having a maximum pH of about 8 containing filler and 0-8% by weight water, and about 1-10% trichlorotoluene and about 20-80% metal salt, selected from the class consisting of SnCl.sub.4, ZnCl.sub.2 and AlCl.sub.3, based on the weight of said monomer, which comprises mixing aggregates in wet or frozen form with the metal salt, separately mixing the furfuryl alcohol monomer with the trichlorotoluene, and then mixing said aggregate mixture with said monomer mixture at ambient temperatures within the range of about -20.degree. C. to about 40.degree. C. to effect polymerization of said monomer in situ within one hour and recovering a polymer concrete having a one hour compressive strength above 2000 psi.