Back to results
US 4,361,606 AGranted
Method for irradiation of polymeric laminates and product
AssigneeMonsanto Company
InventorsJohn M. Butler, Charles L. D. Chin
Life of this patent
Estimating the term…
Loading patent…
Loading patent…
AssigneeMonsanto Company
InventorsJohn M. Butler, Charles L. D. Chin
Estimating the term…
Three-dimensional laminates having improved ductility and resistance to cracking at low temperatures are produced by subjecting the formed laminates to high energy ionizing radiation to preferentially promote crosslinking in at least one layer of the laminate which layer per se has poor low temperature properties. In the preferred form a laminate useful in producing spray reducing rain flaps for vehicle tires is provided by irradiating a fusion bonded laminate comprising a three-dimensional grasslike layer of high melt index, low density polyethylene and a high density polyethylene substrate at an average dose of at least about 10 and preferably about 30 megarads. The resulting rain flap remains ductile at temperatures down to at least about minus 20.degree. F. (minus 29.degree. C.) and preferably minus 40.degree. F. (minus 40.degree. C.).
A process for improving the low temperature ductility of a fusion bonded three-dimensional laminate comprising a grass-like three-dimensional layer of low density polyethylene fusion bonded to a high density polyethylene substrate, said process comprising subjecting said laminate to an average dose of at least about 10 megarads of high energy ionizing radiation to provide a laminate which remains ductile at temperatures down to at least about minus 20.degree. F. (minus 29.degree. C.).
A process for minimizing the tendency of a fusion bonded laminate comprising at least one radiolytically crosslinkable polymeric layer having poor low temperature ductility and at least one polymeric substrate layer having good low temperature ductility to crack through its thickness upon the application of stress at low temperature, said process comprising subjecting said laminate to an average dose of at least about 10 megarads of high energy ionizing radiation to reduce the incidence of crack propagation across the boundary between said layer having poor low temperature ductility and said layer having good low temperature ductility, one said layer being high density polyethylene and the other said layer being low density polyethyelene.
A spray-suppression device comprising a three-dimensional layer of radiolytically crosslinked polymer having multiple discrete portions protruding from the base plane of the layer and being fusion bonded to at least one polymeric substrate layer, said laminate having been irradiated with at least about 10 megarads of high energy radiation and remaining ductile at temperatures down to at least about minus 20.degree. F. (minus 29.degree. C.).
A spray suppression device comprising a grass-like three-dimensional layer of low density polyethylene fusion bonded to a high density polyethylene substrate, said spray suppression device having been subjected to high energy ionizing radiation in an amount sufficient to provide a spray suppression device which remains ductile at temperatures down to at least about minus 20.degree. F. (minus 29.degree. C.).