Glass-encapsulated magnetic materials and methods for making them
AssigneeCorning Glass Works
InventorsNicholas F. Borrelli, David L. Morse, Jan W. H. Schreurs
Life of this patent
Estimating the term…
Abstract
Magnetic materials exhibiting ferrimagnetic and/or superparamagnetic behavior, produced by impregnating porous glasses with iron and, optionally, manganese, cobalt and nickel compounds, reacting the compounds with the porous glass to form bound complexes, heating the glass to expel unreacted organometallics, and further heating to convert the bound complexes to ferrimagnetic and/or superparamagnetic oxide crystallites, are described. Ferrimagnetic iron oxide crystallites exhibiting coercivities above 10,000 Oe can be made.
Claims11
A ferrimagnetic material consisting of ferrimagnetic iron oxide crystallites dispersed in a glass matrix, the crystallites being selected from the group consisting of gamma-Fe.sub.2 O.sub.3, Fe.sub.3 O.sub.4, and mixtures or solid solutions thereof, said crystallites having a maximum diameter not exceeding about 0.05 microns and said material having a coercivity of at least about 1000 Oe at 25.degree. C.
A method of making a ferrimagnetic material which comprises the steps of:
- impregnating a porous glass with an organometallic iron compound;
- reacting the iron compound with the pore walls of the porous glass at a temperature below the thermal decomposition temperature of the iron compound;
- and heating the glass to a temperature at least sufficient to expel unreacted iron compound from the glass and convert the iron in the glass to iron oxide.
A method of making a superparamagnetic material which comprises the steps of:
- impregnating a porous glass with an organometallic iron compound and at least one compound selected from the group consisting of organometallic manganese, nickel and cobalt compounds;
- reacting the compounds with the pore walls of the porous glass at a temperature below the thermal decomposition temperatures of the compounds;
- and heating the glass to a temperature at least sufficient to expel unreacted organometallic compounds from the glass and to convert the metals therein to metal oxides.