Mixed polyvalent-monovalent metal coating for carbon-graphite fibers
AssigneeThe United States of America as represented by the Administrator of the National Aeronautics and Space Administration
InventorsJan Harper-Tervet, Fred W. Tervet, Marshall F. Humphrey
Life of this patent
Estimating the term…
Abstract
An improved coating of gasification catalyst for carbon-graphite fibers is provided comprising a mixture of a polyvalent metal such as calcium and a monovalent metal such as lithium. The addition of lithium provides a lighter coating and a more flexible coating when applied to a coating of a carboxyl containing resin such as polyacrylic acid since it reduces the cross-link density. Furthermore, the presence of lithium provides a glass-like substance during combustion which holds the fiber together resulting in slow, even combustion with much reduced evolution of conductive fragments. The coated fibers are utilized as fiber reinforcement for composites.
Claims11
A composition of matter comprising:
- 30% to 70% by weight of graphite fibers coated with 0.1 to 10% by weight of the fibers of a gasification catalyst comprising a mixture of a monovalent alkali metal salt and polyvalent alkaline earth metal salt having a work function below 4.2 eV;
- said monovalent metal salt comprising 5 to 95% by weight of said mixture;
- and
- the remainder consisting essentially of binder resin and said coated fibers being embedded and dispersed in said binder resin.
A method of forming a composite containing gasifiable graphite fiber comprising the steps of:
- applying a solution containing a mixture of salts of a monovalent alkali metal salt and a polyvalent alkaline earth metal salt, both said metals having a work function below 4.2 eV to the exterior surface of a fine graphite fiber having a diameter from 1 to 30 microns to form gasification catalyst on the fiber in an amount from 0.05 to 20% by weight of the fiber and consisting of 5 to 95% by weight of said monovalent metal;
- dispersing 30 to 70% by weight of the coated fibers in a binder resin;
- and
- curing the resin to form a composite.
Dependencies are inferred from the claim text.