Manganese steels
AssigneeUniversity College Cardiff
InventorsRobert D. Jones, Vijay Jerath
Life of this patent
Estimating the term…
Abstract
This invention relates to manganese steels, in particular the invention relates to high strength iron-manganese based maraging-type steel combining high strength and toughness. Specifically, a manganese steel in accordance with the invention contains, apart from impurities, 11.8-13.5% by weight manganese, 2.0-6.0% by weight molybdenum, 0.002-0.2% by weight carbon, and optionally one or more of silicon (up to 0.4% by weight), sulphur (up to 0.02% by weight), and phosphorus (up to 0.03% by weight), and balance iron.
Claims4
A manganese steel consisting essentially of apart from impurities, 11.8-13.5% by weight manganese, 2.0-6.0% by weight molybdenum, 0.002-0.2% by weight carbon, and optionally one or more of silicon (up to 0.4% by weight), sulphur (up to 0.02% by weight) and phosphorus (up to 0.03% by weight) and balance iron.
Dependencies are inferred from the claim text.