Method for making a stress-relieved composite foamed resin baseball bat or bowling pin
AssigneeMueller-Perry Co., Inc.
InventorAlvin W. Mueller
Life of this patent
Estimating the term…
Abstract
Composite bowling pins and baseball bats are formed with foamed, cured-in place plastic bodies securely adhered to a central aluminum core by a somewhat thermoplastic adhesive coating. The exothermic reaction attendant to curing the plastic so softens the adhesive coating that it does not interfere with shrinkage of the plastic body relative to the core. This minimizes stress concentrations in the composite construction which otherwise tend to lead to cracking in use.
Claims4
The method of making a molded composite baseball bat, bowling pin or like article having a body of cured-in-place foam plastic of a type which has an exothermic reaction and shrinks on curing comprising the steps of
- coating an elongated aluminum core with an adhesive of the type which at least partly softens at the temperature of such exothermic reaction and which at room temperature will securely bond foamed plastic to said core
- causing said coating to dry,
- mounting said coated core within a mold,
- foaming plastic material thereabout within the mold and causing such exothermic reaction,
- softening the dry adhesive coating on the core with the heat of such exothermic reaction,
- permitting the foamed plastic to shrink and draw together slippingly along the softened adhesive coating on the core, and
- thereafter permitting the adhesive coating to harden during cooling of said foamed plastic,
- whereby to minimize stresses which would otherwise accompany resistance of the core to the shrinking of the plastic.
A method of making a baseball bat or bowling pin having a foam plastic body and the use characteristics of a wooden counterpart comprising the steps:
- (a) of coating a tubular, high yield strength aluminum core with a liquid coating composition containing a rubbery polymer of butadiene and acrylonitrile as an essential ingredient, said core having a diameter of from about 0.75 to about 1 inch, a wall thickness of from about 0.06 to about 0.125 inch and a yield strength of at least 30,000 p.s.i.;
- (b) removing substantially all of the liquid components of said composition from the coating;
- (c) positioning the dry coated core in a mold having an internal cavity shaped in the configuration of the desired bat or pin so that the long axis of the core is substantially coincident with the long axis of the bat or pin;
- (d) introducing into the mold cavity a foam plastic precursor which reacts under exothermic conditions to create a temperature above the softening temperature of said coating and to form a foam plastic body which is free to shrink along the axis of said core during cooling without substantially adhering to said coating, the amount of said plastic precursor employed being controlled to provide a foam plastic body having a density of from about 30 to about 50 pounds per cubic foot;
- and
- (e) removing the thus formed bat or pin from said mold.
Dependencies are inferred from the claim text.