Process for producing modified alumina hydrate crystals
AssigneeVereinigte Aluminium-Werke Aktiengesellschaft
InventorsJorg F. Greber, Gunter Winkhaus
Life of this patent
Estimating the term…
Abstract
The present invention relates to a modified form of alumina hydrate filler, thermosetting and thermoplastic compositions having improved workability and mechanical properties containing such filler and methods of manufacturing such modified alumina hydrate filler. More specifically, the invention provides for the admixture of modified alumina hydrate crystals with a resinous composition in which the individual alumina hydrate crystal edges are substantially rounded, have a mean crystal size of less than about 35 microns and less than about 0.1% by volume of alumina hydrate crystals have a diameter of less than 2 microns. The resulting compositions have improved viscosity properties and exhibit good bending strength and flame retardant characteristics.
Claims8
A process for producing modified gibbsite alumina trihydrate particles which comprises:
- stirring a Bayer process lye solution which contains caustic lye and dissolved aluminum oxide to obtain a slightly supersaturated solution and subsequently heating said solution to a sufficient temperature to convert it to an undersaturated state, adding to said undersaturated solution a predetermined amount of gibbsite alumina trihydrate crystals to form a suspension and maintaining said suspension for a sufficient time to convert said crystals to modified particles, said crystals having a mean crystal diameter of between about 40 and 100 microns and having substantially sharp edges and rough surfaces, said modified particles having a mean particle diameter of less than about 35 microns and less than about 0.1 percent by volume of said particles having a diameter of less than about 2 microns, said particles further having substantially rounded edges and smooth surfaces.
A process for producing modified gibbsite alumina trihydrate particles which comprises:
- providing a Bayer process lye composition containing from about 135 to about 140 grams per liter of caustic lye, from about 73 to about 75 grams per liter of aluminum oxide and from about 500 to 600 grams per liter of gibbsite alumina trihydrate crystals in a container, to form a suspension of undissolved crystals heating the suspension of undissolved crystals at a temperature between about 98.degree. C. to about 102.degree. C. for a predetermined period of time and agitating said heated suspension for a second predetermined period of time to form said modified particles, wherein said crystals have a mean crystal diameter between about 40 and 100 microns and have substantially sharp edges and rough surfaces and said modified particles have a mean particle diameter of less than about 35 microns with less than 0.1 percent by volume of said particles having a diameter of less than about 2 microns, said particles further having substantially rounded edges and smooth surfaces.
A process for producing modified gibbsite alumina trihydrate particles which comprises:
- providing a Bayer process lye suspension containing from about 100 to about 200 grams per liter of caustic and about 50 to about 200 grams per liter of dissolved aluminum oxide stirring the suspension to produce a suspension of aluminum hydroxide crystals in a slightly supersaturated Bayer process lye, heating said suspension to provide an aluminum undersaturated solution and maintaining the suspension for a predetermined period of time at a temperature between about 85.degree. C. and 105.degree. C. to convert said crystals to said particles, wherein said crystals have a mean diameter of between 40 and 100 microns and have substantially sharp edges and rough surfaces and said modified particles have a mean particle diameter of less than about 35 microns and less than about 0.1 percent by volume of said particles have a diameter of less than about 2 microns, said particles further having substantially rounded edges and smooth surfaces.