Silicone compositions for the treatment of glass fibers and methods of treatment
AssigneeToray Silicone Company, Ltd.
InventorsTakao Matsushita, Kazuo Hirai
Life of this patent
Estimating the term…
Abstract
A product obtained by mixing a vinyl-containing poly- diorganosiloxane, an organohydrogenpolysiloxane, a silica filler treated with dimethyldichlorosilane, optionally diphenylsilanediol, and a platinum catalyst is useful for treating glass fiber and is an electrical insulating material. The cured product has excellent electrical characteristics, flame retardancy, mechanical strength, and transparency.
Claims21
A silicone composition consisting essentially of a product obtained by mixing
- (A) 100 parts by weight of a triorganosiloxy endblocked polydiorganosiloxane in which each organic group is selected from methyl, vinyl, and phenyl, there being at least two vinyl groups per molecule, there being no more than 20 mol percent phenyl groups based on the total number of moles of organic groups in the polydiorganosiloxane and said polydiorganosiloxane having a viscosity of at least 0.1 m.sup.2 /s measured at 25.degree. C.
- (B) an amount of organohydrogenpolysiloxane sufficient to provide at least 1.5 silicon-bonded hydrogen atoms per vinyl group in (A), said organohydrogenpolysiloxane having at least two silicon-bonded hydrogen atoms per molecule, and the organohydrogensiloxane having organic groups selected from methyl and phenyl,
- (C) from 10 to 100 parts by weight of a silica filler having a relative surface area of at least 50 m.sup.2 /g and having been treated with dimethyldichlorosilane for hydrophobicity, and
- (D) a catalytic amount of a platinum catalyst.
1 more element
A method of treating glass fibers comprising
- (I) mixing the following ingredients to make a silicone composition
- (A) 100 parts by weight of a triorganosiloxy endblocked polydiorganosiloxane in which each organic group is selected from methyl, vinyl, and phenyl, there being at least two vinyl groups per molecule, there being no more than 20 mol percent phenyl groups based on the total number of moles or organic groups in the polydiorganosiloxane and said polyorganosiloxane having a viscosity of at least 0.1 m.sup.2 /s measured at 25.degree. C.
- (B) an amount of organohydrogenpolysiloxane sufficient to provide at least 1.5 silicon-bonded hydrogen atoms per vinyl group in (A), said organohydrogenpolysiloxane having at least two silicon-bonded hydrogen atoms per molecule, and the organohydrogensiloxane having organic groups selected from methyl and phenyl,
- (C) from 10 to 100 parts by weight of a silica filler having a relative surface area of at least 50 m.sup.2 /g and having been treated with dimethyldichlorosilane for hydrophobicity, and
- (D) a catalytic amount of a platinum catalyst,
- (II) dispersing the silicone composition obtained in step
- (I) in an organic solvent to make a treatment solution,
- (III) coating glass fibers with the treatment solution obtained in step (II) to make treated glass fibers, and
- (IV) heating the treated glass fibers to cure the silicone composition
6 more elements
Dependencies are inferred from the claim text.