Integrated process for thermal cracking of heavy oil and reduction of iron ores
AssigneesKobe Steel, Ltd., Koa Oil Company, Limited
InventorsKenji Mori, Eiji Miura, Reijiro Nishida, Kiyohiko Koizumi
Life of this patent
Estimating the term…
Abstract
Vacuum distillation residue oil having a Conradson carbon value of 5 to 40% and a specific gravity of 0.9 to 1.10 is thermally cracked in the presence of iron ore particles in fluidized state in a thermal cracking reactor thereby to produce light oils and cracked gases and to form by-product carbon, which is caused to deposit on the iron ore particles, which are then transferred to and heated at 800.degree. C. to 1200.degree. C. in a reducing furnace to be reduced in a solid state reaction, into sponge iron. Thus, heavy oil is thermally cracked and sponge iron is produced by an economical, integrated process.
Claims7
An integrated process for thermal cracking of hydrocarbon oil and production of iron which consists essentially of:
- (a) thermally cracking the hydrocarbon oil in the presence of iron ore particles of a particle size suitable for fluidization in a fluidized state in a thermal cracking reactor at a temperature of from 400.degree. C. to 630.degree. C. thereby to produce and recover light oils and cracked gases;
- at the same time causing by-product carbon thus formed to deposit on the iron ore particles;
- said hydrocarbon oil being a vacuum distillation residue oil having a Conradson carbon value of 5 to 40 percent and a specific gravity of 0.9 to 1.10 and,
- (b) introducing said carbon-deposited iron ore with or without additional carbon, into a reducing furnace and heating the thus introduced mixture of the carbon deposited iron ore with or without the additional carbon at a temperature of from 800.degree. C. to 1,200.degree. C. in the reducing furnace, while maintaining said mixture in the solid state, to thereby produce sponge iron.
Dependencies are inferred from the claim text.