Bearing material and method of making
AssigneeGould Inc.
InventorLee A. Swanger
Life of this patent
Estimating the term…
Abstract
A process for making a multilayer bearing material is provided which comprises a backing layer, an intermediate layer of aluminum and an outer overlay layer. The backing layer and aluminum layer are roll bonded together to form a composite strip which is then fed into a molten bath of overlay material which provides for good adhesion to the aluminum and also for good bearing material properties. The aluminum surface of the composite is then cleaned to remove surface oxide and the composite is removed from the bath into a guide means and through a gate which controls the thickness of the overlay so that upon solidification of the molten overlay material a finished bearing material is produced. The fusion bonding of overlay material to the composite is performed in a single operation.
Claims11
A method for producing a multilayer metallic bearing material which has an interlayer of aluminum or aluminum-base alloy comprising:
- providing a composite strip of a backing material bonded to said aluminum or aluminum-base alloy;
- passing the composite strip below the surface of a bath of a molten bearing overlay material;
- removing surface oxide from the surface of the aluminum or aluminum-base alloy layer while under the surface of the bath thereby allowing uniform adherence of the molten overlay material to the aluminum or aluminum-base alloy interlayer;
- and
- withdrawing the composite strip from the bath and simultaneously controlling uniform thickness of the overlay material on the interlayer over the width of the strip thereby providing the bearing material with bonded overlay layer of the ultimate bearing surface material upon solidification without the need of further casting step.
A method for producing a multilayer metallic bearing which has an interlayer of aluminum or aluminum-base alloy comprising:
- providing a composite strip of a backing material bonded to said interlayer;
- passing the composite strip below the surface of a bath of molten bearing overlay material of an alloy of lead and tin and at least one metal chosen from the group consisting of zinc, cadmium and copper;
- removing surface oxide from the surface of the interlayer while under the surface of the bath thereby allowing uniform adherence of the molten overlay material to the interlayer;
- withdrawing the strip from the bath and simultaneously controlling uniform thickness of the overlay material on the interlayer over the width of the strip thereby providing a bearing material with bonded overlay layer of the ultimate bearing surface material upon solidification without the need of further casting step;
- forming the composite strip with overlay layer into bearing shell.
A method for producing a multilayer metallic bearing material which has a layer of aluminum or aluminum-base alloy comprising:
- providing a strip having at least one surface of aluminum or aluminum-base alloy;
- passing said strip below the surface of a bath of a molten bearing overlay material;
- removing surface oxide from the surface of the aluminum or aluminum-base alloy layer while under the surface of the bath thereby allowing uniform adherence of the molten overlay material to the aluminum or aluminum base-alloy layer;
- and
- withdrawing the strip from the bath and simultaneously controlling uniform thickness of the overlay material on the aluminum or aluminum-base alloy layer over the width of the strip thereby providing the bearing material with bonded ultimate overlay layer of the ultimate bearing surface material upon solidification without the need of further casting step.