Producing reticulated thermoplastic rubber products

Process for producing reticulated thermoplastic rubber sheet material which comprises:

• (a) extruding a thin molten sheet consisting essentially of a mixture of
• (i) thermoplastic rubber comprising a block copolymer of styrene and butadiene or isoprene, and
• (ii) sufficient olefin polymer to improve the processability of said thermoplastic rubber, as evidenced by the ability to achieve a draw ratio of greater than 1 while extruding said mixture, said olefin polymer being selected from the group consisting of isotactic polypropylene, polyethylene, amorphous polypropylene, polybutylene, ethylene/vinyl acetate copolymer, ethylene/ethyl acrylate copolymer, ethylene/methyl acrylate copolymer, and polystyrene;
• (b) feeding the extruded molten sheet directly to the surface of a smooth surfaced first roll at a first position on said surface, wherein said first roll is rotating at a first peripheral linear speed, wherein said first roll is in contact with a second roll at a second position on said surface disposed from said first position to form a nip between said first and second rolls, the second roll havings its longitudinal axis essentially parallel to the longitudinal axis of the first roll, wherein said second roll is rotating in a direction opposite to said first roll at a second peripheral linear speed equal to, slightly greater, of slightly less than said first peripheral linear speed, and wherein said second roll has a resilient surface with a pattern of continuous recessed areas and discontinuous raised areas disposed over its surface;
• (c) passing said molten sheet from said first position to said second position, with the surface temperature of said first roll being such that said sheet is in a formable state when it arrives at said second position;
• (d) passing said sheet through the nip between said first and second rolls, wherein the pressure at said nip is sufficient to penetrate said sheet and form said sheet into an open reticulated sheet of intersecting filaments corresponding in structure to said pattern of recessed areas on the surface of said second roll;
• (e) passing said open reticulated sheet around the surface of said second roll to a third position on the surface of said second roll disposed from said nip, wherein the surface of said second roll is maintained at a temperature such that said reticulated sheet is a solid, self-supporting structure when it arrives at said third position;
• and
• (f) removing said reticulated sheet from said second roll at said third position.